Effect of Water/Binder Ratio on Cementation of Radioactive Spent Resin

SUN Qi-na,LI Jun-feng,WANG Jian-long

2012-01-01

Abstract:Simulated radioactive spent resins were solidified by sulfoaluminate cement,and the influence of water/binder ratio and the blending amount of naphthalene-based water reducer UNF-5 on fluidity,setting times and compressive strength of waste forms were investigated.With water/binder ratio increasing from 0.25 to 0.35,the fluidity enhances linearly from 228 mm to 280 mm.The initial and final setting time prolong from 3.0 h and 9.3 h to 4.6 h and 10.4 h,respectively.The 28 d compressive strength decreases linearly from 19.8 MPa to 13.5 MPa.When the blending amount of UNF-5 increases,the fluidity increases,the setting time decreases initially and then increases,and the compressive strength increases to the maximum and then decreases.With UNF-5 blending amount of 0.05%-0.10%,the fluidity is 200-225 mm,the initial and final setting time are 3-4 h and 11-12 h,respectively,and the 28 d compressive strength is 21.1-21.7 MPa.