Solidification of Borate Radioactive Resins Using Sulfoaluminate Cement Blending with Zeolite

Qina Sun,Junfeng Li,Jianlong Wang

DOI: https://doi.org/10.1016/j.nucengdes.2011.08.028

IF: 1.7

2011-01-01

Nuclear Engineering and Design

Abstract:The solidification of borate radioactive resins using sulfoaluminate cement (SAC) blending with zeolite was investigated, and the performance of SAC-zeolite matrix for immobilizing borate resin was evaluated based on the compressive strength, leachability and mineral phases of solidified waste forms. The experimental results showed that the 28 d compressive strength of resin SAC-zeolite waste forms was 18.8 MPa, the cemented waste forms meet the requirement of water, freezing, irradiation and impact resistance tests. The leaching processes of Cs+ and Co2+ were diffusion-limit step. The leachability of Cs+ was higher than Co2+ no matter what the matrix contained zeolite or not, but leachability of both cations was reduced by adding 5% zeolite. For SAC-zeolite matrix, the leaching rates of Cs+ and Co2+ were 6.40 x 10(-5) cm/d and 1.62 x 10(-7) cm/d, and the cumulative leaching fractions were 2.9 x 10(-3) cm and 2.3 x 10(-5) cm. respectively. The X-ray diffraction (XRD) analysis suggested that B(OH)(4)(-) was incorporated by substitution of SO4- in the crystalline structure of ettringite (3CaO center dot Al2O3 center dot 3CaSO(4)center dot 32H(2)O). (C) 2011 Elsevier B.V. All rights reserved.