Solidification of radioactive spent liquid scintillator wastes: Effect of additives on the compressive strength of the solidified forms

Lei Chen,Junfeng Li,Jianlong Wang

DOI: https://doi.org/10.1016/j.nucengdes.2024.112932

IF: 1.7

2024-01-24

Nuclear Engineering and Design

Abstract:The safe disposal of radioactive spent liquid scintillator wastes is still a challenge. In this study, the solidification of the spent liquid scintillator wastes was investigated using ordinary Portland cement and sulfoaluminate cement, focusing on the improvement of the compressive strength of the solidified forms by different additives, including zeolite and nano-SiO 2 . The feasibility and effect of ordinary Portland cement and sulfoaluminate cement as the matrix material for solidifying liquid scintillator wastes was compared. The setting time of ordinary Portland cement was too long for solidifying the liquid scintillator wastes, while the setting time of Sulfoaluminate cement was suitable. The influence and the addition range of zeolite and nano-SiO 2 as additives was studied as well. Adding 0 ∼ 3 wt% zeolite could improve the compressive strength of the SAC solidified forms, and the highest compressive strength (16.6 MPa) was obtained with addition of 3 wt% zeolite, 15.3 % higher than that without zeolite. The addition of 1 ∼ 3.5 wt% nano-SiO 2 could increase the compressive strength of the SAC solidified forms, and the highest compressive strength (16.5 MPa) was obtained with addition of 3 wt% nano-SiO 2 , 13.5 % higher than that without nano-SiO 2 . The compressive strength of the SAC solidified forms meets the requirement of GB 14569.1–2011. Zeolite and nano-SiO 2 could significantly improve the compressive strength of the solidified forms, suggesting that they are feasible and effective as an additive for cementation of the radioactive liquid scintillator wastes.

nuclear science & technology