Low leaching characteristics and encapsulation mechanism of Cs+ and Sr2+ from SAC matrix with radioactive IER

Xingang Xu,Haifeng Bi,Yang Yu,Xinghua Fu,Shoude Wang,Yu Liu,Pengkun Hou,Xin Cheng

DOI: https://doi.org/10.1016/j.jnucmat.2020.152701

IF: 3.555

2021-02-01

Journal of Nuclear Materials

Abstract:Radioactive ion exchange resin is a problematic waste requiring proper immobilization to ensure that the resin's radioactive ions are stable for storage and ultimate disposal in water environments, such as seawater or groundwater. Sulphoaluminate cement hardened paste, with the dense structure, great retention capacity for ions, and resistance to SO4 2− and Cl−, is a potential cementation material to encapsulate 137Cs+ and 90Sr2+ in radioactive ion exchange resin. The leaching rates of Cs+ and Sr2+ from the sulfoaluminate cement matrix solidifying radioactive ion exchange resin and their immobilization characteristics of the predominant hydration products (ettringite; aluminum hydroxide gel) of sulfoaluminate cement were investigated in depth. The experimental results showed that the sulphoaluminate cement radwaste matrix had a better retention capacity for Cs+ and Sr2+ than the OPC radwaste matrix. The 42 days cumulative leaching fractions of Cs+ and Sr2+ were 6.21 × 10−2 and 5.77 × 10−3 cm, respectively, which could be described by the FRDM or DDIM model for Cs+, and the DDIM model for Sr2+. The retention of Cs+ and Sr2+ originated from the chemical absorption by ettringite, aluminum hydroxide gel, and the physical barrier. The ettringite and aluminum hydroxide gel's retention rates for Cs+ are above 70% and 40%, respectively, while those of Sr2+ are above 88% and 10%, respectively. In detail, Cs+ and Sr2+ could be absorbed by both ettringite and aluminum hydroxide gel. Unlike Cs+, Sr2+ could enter the ettringite's crystal lattice by replacing Ca2+ and entering the negative channel.

materials science, multidisciplinary,nuclear science & technology

What problem does this paper attempt to address?

The problem that this paper attempts to solve is the stabilization and solidification of radioactive waste generated by radioactive ion - exchange resins (IER) in pressurized water reactor (PWR) nuclear power plants. Specifically, the research focuses on how to effectively encapsulate and stabilize radioactive cesium ($\text{Cs}^+$) and strontium ($\text{Sr}^{2+}$) using sulphoaluminate cement (SAC) to reduce the leaching rates of these radioactive ions in the water environment, thereby ensuring long - term safe storage and final disposal.

### Research Background
Radioactive ion - exchange resin is an important nuclear waste, containing $\text{Cs}^+$ and $\text{Sr}^{2+}$, and appropriate solidification methods are required to ensure its stability in the water environment. Currently, commonly used solidification methods include cement solidification, bituminization and vitrification. However, bituminization and vitrification require high - temperature treatment and are prone to causing fires, so cement solidification is the most widely used technique.

### Research Objectives
1. **Evaluate the solidification performance of sulphoaluminate cement (SAC)**: Research the solidification effect of SAC on $\text{Cs}^+$ and $\text{Sr}^{2+}$, especially its performance compared with ordinary Portland cement (OPC).
2. **Analyze the solidification mechanism**: Explore the immobilization mechanisms of $\text{Cs}^+$ and $\text{Sr}^{2+}$ in the SAC solidification matrix, including physical fixation and chemical adsorption.
3. **Establish a leaching model**: Fit different mathematical models through experimental data to determine the leaching behaviors of $\text{Cs}^+$ and $\text{Sr}^{2+}$.

### Main Research Contents
1. **Sample Preparation**:
- Prepare a cement matrix using SAC and simulated radioactive ion - exchange resin.
- The simulated radioactive ion - exchange resin is prepared by soaking in $\text{CsCl}$ and $\text{SrCl}_2$ solutions.
2. **Testing Methods**:
- **Leaching Test**: Conduct a leaching test according to the GB/T 7023 - 2011 standard to measure the leaching rates and cumulative leaching fractions of $\text{Cs}^+$ and $\text{Sr}^{2+}$.
- **Pore Structure Analysis**: Analyze the pore structures of SAC and OPC matrices using mercury intrusion porosimetry (MIP).
- **Chemical Analysis**: Analyze the chemical components and microstructures of the solidified matrices using techniques such as ICP - MS, FT - IR, and SEM - EDS.
3. **Results and Discussion**:
- **Leaching Performance**: The leaching rates of $\text{Cs}^+$ and $\text{Sr}^{2+}$ in the SAC matrix are significantly lower than those in the OPC matrix, indicating that SAC has a better solidification effect.
- **Leaching Model**: By fitting models such as Fick's second law, FRDM, and DDIM, the leaching mechanisms of $\text{Cs}^+$ and $\text{Sr}^{2+}$ are determined. The leaching of $\text{Cs}^+$ in the SAC matrix is mainly controlled by diffusion, while the leaching of $\text{Sr}^{2+}$ is mainly affected by both dissolution and diffusion.
- **Solidification Mechanism**: The dense microstructure and high mechanical properties of the SAC matrix help to reduce ion leaching. In addition, the hydration products of SAC, such as ettringite and aluminum hydroxide gel (AHG), have good adsorption capacities for $\text{Cs}^+$ and $\text{Sr}^{2+}$.

### Conclusion
Sulphoaluminate cement (SAC) exhibits excellent performance in solidifying radioactive ion - exchange resins, especially in reducing the leaching rates of $\text{Cs}^+$ and $\text{Sr}^{2+}$. The solidification mechanism of SAC includes physical fixation and chemical