Tungsten Modified MnOx–CeO2/ZrO2 Monolith Catalysts for Selective Catalytic Reduction of NOx with Ammonia
Haidi Xu,Qiulin Zhang,Chuntian Qiu,Tao Lin,Maochu Gong,Yaoqiang Chen
DOI: https://doi.org/10.1016/j.ces.2012.04.012
IF: 4.7
2012-01-01
Chemical Engineering Science
Abstract:A series of WO3–ZrO2 carriers were prepared by co-precipitation method with different mass fractions (0wt%, 5wt%, 10wt%, 15wt% and 20wt%) of WO3, and MnOx–CeO2/WO3–ZrO2 monolith catalysts were prepared for selective catalytic reduction of NOx with ammonia (NH3-SCR) in the presence of excessive O2. The catalysts were characterized by N2 adsorption–desorption, X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and NH3/NO temperature-programmed desorption (NH3/NO-TPD). The experimental results showed that, the tungsten modified monolith catalyst MnOx–CeO2/WO3–ZrO2 with the WO3 content 10wt% had the best catalytic activity and the widest reaction window; it possessed a better thermal stability than V2O5/WO3/TiO2 catalyst, and showed a better H2O and SO2 tolerance than MnOx–CeO2/ZrO2. The characterization results indicated that MnOx–CeO2/10% WO3–ZrO2 had the best textural properties, a well-dispersed state of WO3, the lowest binding energy of Ce3+ 3d5/2, the maximum value of Ce3+:Ce=20.7%, the suitable molar ratio of Mn:Ce≈1, and a co-existence state of MnO2–Mn2O3. In addition, it had the most adsorbed sites of NH3 or NO species. The NOx conversion was more than 80% in the temperature range of 150°C to 380°C at the space velocity of 10,000h−1. It possessed better potential for practical application.