Abstract:Red mud, which could cause numerous problems to the environment, is a hazardous waste generated from the alumina smelting industry. In general, the storage and harmless utilization of red mud are hard to implement due to its fine particle size and high alkalinity. This study put forward a novel process to separate iron (MgFe2O4) and alumina (Al2O3) in red mud by a magnetization sintering method. The magnesium oxide was added to transform the nonmagnetic Fe2O3 into magnetic MgFe2O4 to achieve physical separation of iron-bearing minerals, and the alumina-bearing minerals were converted into dissoluble NaAlO2 minerals in a one-step reaction. The atmospheric pressure leaching process was adopted in this study for alumina resource recovery. To achieve clean alumina production, the silicate in the leaching solution was removed by adding the slightly soluble CaSO4, and the entire process becomes clean and harmless. The feasibility of the process was verified by thermodynamic analysis, and a series of experiments were performed to detect the optimum MgO/(Fe2O3 + MgO) ratio and the calcining and leaching conditions. The morphological and mineralogical characteristics of modified red mud, leaching red mud, and magnetic separation product were studied by X-ray diffraction analysis (XRD) and scanning electron microscopy (SEM) energy dispersive spectroscopy (EDS). It was observed that under the optimal conditions with MgO/(Fe2O3 + MgO) of 14.89% to recover iron and aluminum, the corresponding recovery rates were 67.54% and 73.01% respectively, and the iron grade was 30.46%. The EDS results showed that the obtained Mg/Fe ratio of the magnetic separation product was 0.4677–0.528, which is slightly different from that of the standard MgFe2O4 at 0.5. This new method can promote the development of comprehensive utilization of red mud and iron production.

Effect of Fluidized Separating-Washing of Red Mud on Secondary Reactions of Leached Slurry with High Alumina Concentration

Extraction of Aluminum and Preparation of Polymerized Aluminum Ferric Sulfate from Red Mud

Extraction of Iron and Alumina from Red Mud with a Non-Harmful Magnetization Sintering Process

Study on Leaching at the Early Stage of Highly Efficient Flocculants

Fluidization Washing of the Red Mud

Leaching Kinetics and Reactivity Regulation of Red Mud in an NaOH Solution

High‐efficiency Preparation of Fe–Al Based Flocculants from Red Mud by Microwave Selective Carbothermic Reduction and Magnetic Separation

Alumina Recovery from Red Mud with High Iron by Sintering Process

Study on Dealkalization and Settling Performance of Red Mud

Preparation and Application of Polyaluminum Ferric Sulfate from Red Mud: Behaviors of Leaching, Polymerizing, and Coagulation

Research of Leaching Alumina and Iron Oxide from Bayer Red Mud

Comprehensive Recovery of Iron and Aluminum from Ordinary Bayer Red Mud by Reductive Sintering–Magnetic Separation–Digesting Process

A New Route for Separation and Recovery of Fe, Al and Ti from Red Mud

Research of Flocculants and Dewatering Additives for Filtration of Red Mud

Simultaneous Extraction of Fe, Al, Sc and Cr from Red Mud by Ammonium Sulfate Calcination in the Range 250–400°C

Clean dealkalization technology from aluminum industry hazardous tailings—red mud by displacement with Mg-based agent

Extracting Al2O3 and TiO2 from Red Mud Smelting Separation Slag by Alkali and Acid Leaching Methods

Removal of Alkali in the Red Mud by So2 and Simulated Flue Gas under Mild Conditions

Recovery of Alumina and Ferric Oxide from Bayer Red Mud Rich in Iron by Reduction Sintering

Iron Extraction from Red Mud using Roasting with Sodium Salt

Study on particle-size separation pretreatment of Bayer red mud