Abstract:Red mud, which could cause numerous problems to the environment, is a hazardous waste generated from the alumina smelting industry. In general, the storage and harmless utilization of red mud are hard to implement due to its fine particle size and high alkalinity. This study put forward a novel process to separate iron (MgFe2O4) and alumina (Al2O3) in red mud by a magnetization sintering method. The magnesium oxide was added to transform the nonmagnetic Fe2O3 into magnetic MgFe2O4 to achieve physical separation of iron-bearing minerals, and the alumina-bearing minerals were converted into dissoluble NaAlO2 minerals in a one-step reaction. The atmospheric pressure leaching process was adopted in this study for alumina resource recovery. To achieve clean alumina production, the silicate in the leaching solution was removed by adding the slightly soluble CaSO4, and the entire process becomes clean and harmless. The feasibility of the process was verified by thermodynamic analysis, and a series of experiments were performed to detect the optimum MgO/(Fe2O3 + MgO) ratio and the calcining and leaching conditions. The morphological and mineralogical characteristics of modified red mud, leaching red mud, and magnetic separation product were studied by X-ray diffraction analysis (XRD) and scanning electron microscopy (SEM) energy dispersive spectroscopy (EDS). It was observed that under the optimal conditions with MgO/(Fe2O3 + MgO) of 14.89% to recover iron and aluminum, the corresponding recovery rates were 67.54% and 73.01% respectively, and the iron grade was 30.46%. The EDS results showed that the obtained Mg/Fe ratio of the magnetic separation product was 0.4677–0.528, which is slightly different from that of the standard MgFe2O4 at 0.5. This new method can promote the development of comprehensive utilization of red mud and iron production.

Alumina Recovery from Red Mud with High Iron by Sintering Process

Recovery of Alumina and Ferric Oxide from Bayer Red Mud Rich in Iron by Reduction Sintering

Comprehensive Recovery of Iron and Aluminum from Ordinary Bayer Red Mud by Reductive Sintering–Magnetic Separation–Digesting Process

Extraction of Iron and Alumina from Red Mud with a Non-Harmful Magnetization Sintering Process

Recovery of Iron from High-Iron Red Mud by Reduction Roasting with Adding Sodium Salt

Iron Extraction from Red Mud using Roasting with Sodium Salt

Recovery of iron and calcium aluminate slag from high-ferrous bauxite by high-temperature reduction and smelting process

Application of Bayer red mud for iron recovery and building material production from alumosilicate residues

Investigation of the smelting reduction mechanism and of iron extraction from high-iron red mud

Recovery of Iron and Titanium in Red Mud with Secondary Aluminum Dross Followed by Manufacturing Glass Ceramics

Experimental and simulative study on phase transformation in Bayer red mud soda-lime roasting system and recovery of Al, Na and Fe

Study and Application of Intensified Sintering Processfor Alumina Production

Kinetics and Mechanism of Red Mud Carbothermic Reduction and Reduced Iron Grain Growth: An Influence of Sodium Sulfate

Alumina-enhanced Valorization of Ferronickel Slag into Refractory Materials under Microwave Irradiation

Carbothermal reduction of red mud for iron extraction and sodium removal

Study on Magnetization Roasting Kinetics of High-Iron and Low-Silicon Red Mud

Reductive roasting of red mud with carbon and sulfuric acid dissolution of iron and aluminum: Transformation phases and leaching characteristics

Size separation pretreatment and alumina recovery from Bayer red mud

Recover Iron From Bauxite Residue (Red Mud)

Recovery of Alkali and Alumina from Bayer Red Mud by the Calcification–carbonation Method

A Case Study of Producing Alumina from High-Sulfur Diasporic Bauxite: Sulfur-Containing Desilication Products and Pyrite in Red Mud