Abstract:The SO2/NOX pollution in the flue gas of non-ferrous smelting is increasingly serious. At the same time, the accumulation of red mud (RM) in the aluminum industry and phosphorus sludge (PS) in the yellow phosphorus industry has caused serious harm to the environment. To remove SO2 and NOX from the non-ferrous smelting flue gas and realize the resource utilization of the above two solid wastes, an ultrasonic field was used in this study to strengthen the PS excited O3 process and RM wet desulfurization and denitrification process. In the process of O3 excitation, the response surface method (RSM) is used to obtain the optimal O3 excitation concentration, and the optimal reaction conditions are designed based on the response surface optimization model: T is 53.226 °C, power density is 0.4 W/cm2, PS concentration is 51.433 g/L, O3 formation concentration up to 250 ppm or more, which provides a theoretical basis for subsequent desulfurization and denitrification steps. It is proved that this study can replace the expensive traditional O3 generator and provide a basis for NOX removal in the following process. In addition, the optimum experimental conditions of ultrasonic enhanced RM desulfurization and denitrification process were also explored. Under ultrasonic frequency of 28 kHz, ultrasonic power density of 0.4 W/cm2, T of 50 °C, RM concentration of 15 g/L, and stirring intensity of 1000 rpm, the desulfurization efficiency of the reaction system can be maintained above 95 % within 250 min, and the denitrification efficiency can be maintained above 90 % within 250 min. The effect of desulfurization and denitrification in this study is much better than that of traditional methods. Finally, the reaction mechanism of ultrasonic enhanced O3 excitation and RM wet desulfurization and nitrogen removal was discussed by combining adsorption thermodynamics, isotherm, and kinetics. The results showed that the OH· free radicals generated by ultrasonic cavitation and the physical effects brought by emulsification had significant promoting effects.

Removal of Alkali in the Red Mud by So2 and Simulated Flue Gas under Mild Conditions

Removal of Alkali in the Red Mud Using Co2 at Ambient Conditions

Dealkalization of Red Mud by Carbide Slag and Flue Gas

Staged characteristics of red mud dealkalization by CO2 and SO2

Characteristics and mechanism of sodium removal by the synergistic action of flue gas and waste solid]

Red mud with enhanced dealkalization performance by supercritical water technology for efficient SO 2 capture

Staged leaching behavior of red mud during dealkalization with mild acid

Clean dealkalization technology from aluminum industry hazardous tailings—red mud by displacement with Mg-based agent

Selective extraction of sodium from red mud by dry digestion

Experimental Study on the Dealkalization of Red Mud Waste from Bayer Process by CO2Gas Floatation

Analysis of Alkali in Bayer Red Mud: Content and Occurrence State in Different Structures

Ultrasonic-enhanced Phosphorus Sludge Excited O3 Coupled Red Mud Simultaneous Desulfurization and Denitrification

An Efficient Dealkalization of Red Mud Through Microwave Roasting and Water Leaching

Study on the Dealkalization Technics of Bayer-process Red Mud with CO_2 by Carbonation

Novel Method for High-Performance Simultaneous Removal of NOx and SO2 by Coupling Yellow Phosphorus Emulsion with Red Mud

An Experimental Study on SO2 Emission and Ash Deposition Characteristics of High Alkali Red Mud under Large Proportional Co-Combustion Conditions in Fluidized Bed

Efficient dealkalization of red mud and recovery of valuable metals by a sulfur-oxidizing bacterium

Leaching Kinetics and Reactivity Regulation of Red Mud in an NaOH Solution

The Research on Ammonium Salt Was Used to Remove Sodium from Fly Ash Red Mud

Enhanced sequestration of CO2 from simulated electrolytic aluminum flue gas by modified red mud

[Inhibition of Sulfite Oxidation Catalyzed by Heavy Metals in Dual Alkali Flue Gas Desulfurization Slurry].