Abstract:Red mud is a solid waste residue from the caustic soda leaching of bauxite ores to produce alumina by the Bayer process. Red mud contains large quantity of alkali and aluminosilicate, so it is potentially available to prepare inorganic polymeric materials by geopolymerisation process. However, the activity or dissolubility of the aluminosilicate phases in red mud is significantly poor, which constraints the geopolymerisation process. Therefore, some pretreatment process for red mud is necessary to improve the adhesive property and dissolubility of Bayer red mud. In this study, mineral phase transformation and dissolubility of a typical red mud sample were studied under different thermal treatment processes. The thermal behavior of the red mud was studied by TG-DTA. The crystalline phases of the samples calcined at 200–1000 °C for different hours were determined by XRD, and the dissolubility was determined by alkaline leaching test. The TG-DTA pattern shows no obvious endothermic or exothermic peaks, and the weight loss increases continuously as the temperature rises, which indicates that the crystalline phases transform continuously as the temperature rises, consistent with the XRD results. As the calcination temperature rises from 200 to 800 °C, several kinds of crystalline phase in original red mud, including gibbsite, katoite, muscovite, natrodavyne disappeared in succession, accompanied with the formation of nepheline, gehlenite, sodium aluminum silicate, and some amorphous aluminosilicate. The calcined products are more likely to dissolve. But when it rises over than 800 °C, the content of gehlenite increases, and the phase of which is stable. As the calcination temperature rises from 200 to 1000 °C, the dissolubility of aluminosilicate in the red mud under high alkaline conditions increases firstly and then decreases after over 800 °C. Therefore, the optimum temperature of thermal treatment for red mud is about 800 °C. This study could contribute to the following preparation of geopolymeric material made from red mud, especially the pretreatment process of red mud.

Study on Dealkalization and Settling Performance of Red Mud

Staged leaching behavior of red mud during dealkalization with mild acid

An Efficient Dealkalization of Red Mud Through Microwave Roasting and Water Leaching

Leaching Kinetics and Reactivity Regulation of Red Mud in an NaOH Solution

Staged characteristics of red mud dealkalization by CO2 and SO2

An Eco-Friendly Acid Leaching Strategy for Dealkalization of Red Mud by Controlling Phase Transformation

Clean dealkalization technology from aluminum industry hazardous tailings—red mud by displacement with Mg-based agent

Study on the effect of sodium removal from citric acid pretreated red mud on the physical properties of red mud

Dealkalization of Red Mud by Carbide Slag and Flue Gas

Selective extraction of sodium from red mud by dry digestion

Removal of Alkali in the Red Mud Using Co2 at Ambient Conditions

Red mud with enhanced dealkalization performance by supercritical water technology for efficient SO 2 capture

Comprehensive Utilization of Red Mud: Current Research Status and a Possible Way Forward for Non-hazardous Treatment

Chemical And Geotechnical Properties Of Red Mud At Liulin, China

Influence of Thermal Treatment on Phase Transformation and Dissolubility of Aluminosilicate Phase in Red Mud

Phase Transformation of Desilication Products in Red Mud Dealkalization Process

Research of Flocculants and Dewatering Additives for Filtration of Red Mud

Removal of Alkali in the Red Mud by So2 and Simulated Flue Gas under Mild Conditions

Comprehensive Utilization of Red Mud Through the Recovery of Valuable Metals and Reuse of the Residue

Settling properties and utilization of red mud produced in Bayer process with an excessive addition lime

Research of Leaching Alumina and Iron Oxide from Bayer Red Mud