Abstract:The hole defects can easily occur in magnesium alloy castings that are prepared by low pressure lost foam casting (LP-LFC) process when the process parameters such as vacuum, pouring temperature and filling velocity are not properly selected. In this study, the forming mechanism of the hole defects in AZ91D magnesium castings by LP-LFC process was investigated. The shape, location and surface appearance of the hole defects were observed using optical microscopy and scanning electron microscopy, and the chemical composition on the surface of the holes was analyzed using energy spectrometer. The result indicates that there are two types of hole defects, i.e., the pyrolysis products related hole defects, including concentrative hole and blow hole defects, and slag related hole defects. The concentrative hole and the blow-hole defects were formed either by the liquid-EPS degradation products entrapped in the molten metal under the condition that the pouring temperature is equal to or lower than 730 ℃, or by the hindered transport of EPS pyrolysis products. Some irregular shape hole defects were caused by slag or by coating slough entrapment when the pouring temperature is equal to 750 ℃ and the filling velocity is equal to or greater than 100 mm·s-1. To reduce or eliminate the hole defects, the vacuum and filling velocity must be properly chosen to ensure that the metal front profile exhibits convex shape and in laminar current state, and the pouring temperature should be just high enough to ensure that the molten melt has adequate heat energy to complete the foam pyrolysis and to fully occupy the mould. For AZ91D magnesium castings in this study, the parameters should be 730 ℃ pouring temperature, 0.02-0.03 MPa vacuum and 80 mm·s-1 filling velocity.

Pressure Solidification Process of Magnesium Alloy in Lost Foam Casting

Influence of Pressure Solidification on AZ91D Magnesium Alloy Feeding in Lost Foam Casting Process

Microstructure And Mechanical Properties Of Magnesium Alloy Prepared By Lost Foam Casting

Low Pressure Lost Foam Process for Casting Magnesium Alloys

Microstructure of AZ91D Magnesium Alloy in Low Pressure Lost Foam Casting

Study on Structure and Corrosion Resistance of AZ91 Magnesium Alloy in Lost Foam Casting Process

Study on the Influencing Factors and Filling Ability of Magnesium Alloys in the Lost Foam Casting(LFC) with Vacuum and Low Pressure

Characteristics of AZ91 Mg-alloy from lost foam casting

Study on Typical Hole Defects in Az91d Magnesium Alloy Prepared by Low Pressure Lost Foam Casting

Study on the Cavity Defects of Low-Pressure Lost Foam Casting for Magnesium Alloy

Study on Mold Filling in AZ91 Alloy LFC Process

Effects of Pressure Field on Structure and Properties of Lost Foam Casting ZL101 Alloy

New Advancements in Research and Application of Al Alloys and Mg Alloys by the Lost Foam Casting Process

Study on Pressurized Solidification Behavior and Microstructure Characteristics of Squeeze Casting Magnesium Alloy AZ91D

Surface Alloying Process Factors of Lost Foam Casting Magnesium Alloy

Heat Transfer Characteristics of Lost Foam Casting Process of Magnesium Alloy

Development of AZ91+X%Cd+Y%MM Magnesium Alloy Prepared by Lost Foam Casting

Fluidity of Magnesium Alloy in Vacuum Low Pressure Lost Foam Casting

Structure and Elemental Composition of Surface Film of Magnesium Alloy Lost Foam Casting

Study on Microstructure and Mechanical Properties of Mg9AlZnGdY Magnesium Alloy after T6 in Lost Foam Casting

Research and Development of EPC Process for Magnesium Alloys