Study on Structure and Corrosion Resistance of AZ91 Magnesium Alloy in Lost Foam Casting Process

Wu Guo-hua,Liu zi-li,FAN Yu,DING Wen-jiang,ZHU Yan-ping

DOI: https://doi.org/10.3321/j.issn:1001-4977.2005.08.009

2005-01-01

Abstract:The microstructure, mechanical properties and corrosion behavior of AZ91 Mg alloy in lost foam casting (LFC) have been studied by metallographic microscope, EDX, electronic universal materials testing machine, weight loss corrosion rate, potentiodynamic polarization and impedance spectroscopy measurements, and were compared with these of ordinary sand mould casting and permanent mould casting. The results show that except for the coarse α and β phases, the ternary Al-Mn-Fe phase also appeared in the microstructure in LFC casting. The lower mechanical properties and corrosion resistance of LFC AZ91 compared with these of ordinary sand mould casting and permanent mould casting were obtained. The experimental results show that the tensile strength and elongation of LFC AZ91 alloy are 135.6 MPa and 1.4% respectively, and its weight loss corrosion rate is 0.64 mg/(cm2·d), 2.2 times that of the permanent mould casting. The research results of potentiodynamic polarization and impedance spectroscopy measurement show that the casting processes have obvious effect on the corrosion behavior of magnesium alloy, and the LFC AZ91 alloy has lower corrosion potential and higher corrosion current density, their values are -1.577 V and 1.39×10 - 5 Amp/cm2, respectively.