Abstract:A simple spray approach to fabricate superhydrophobic coatings on tile and glass substrates is presented. Commercial available polyphenylene sulfide (PPS) and hydrophobic silica (H-SiO(2)) powder were suspended in ethanol and the mixed suspensions were spray on substrates. After dried at different temperatures, surface coatings with different hydrophobicity were obtained. By observing the surface morphologies with scanning electron microscope (SEM) and atomic force microscope (AFM), and measuring water contact angles with a contact angle system, factors affecting the morphology, roughness and contact angle of the surface coatings, such as thermal treatment temperature and the weight ratio of H-SiO(2) to PPS, were investigated in detail. With the increase of the thermal treatment temperature, both the surface roughness and the contact angle increased when the temperature was lower than 280 degrees C. As the weight ratio of H-SiO(2) to PPS rose from 1: 10 to 1:1, more H-SiO(2) powders accumulated on the surface, leading to a significant increase of hydrophobicity. The surface coating obtained at 280 degrees C with the weight ratio of H-SiO(2) to PPS 1:1 showed a water contact angle higher than 150 degrees and a sliding angle lower than 4, exhibiting fascinating superhydrophobic properties. The surface coating could remain superhydrophobicity upon a further increase in thermal treatment temperature or the amount of H-SiO(2) powder. Moreover, the surface coatings showed high contact angles, larger than 150, for all the solutions with pH ranging from 1 to 14. The abrasion resistant property of the as-prepared superhydrophobic surface coating was tested using a homemade setup. Being scraped by freely-falling sands, the superhydrophobic coating could keep its high hydrophobicity, while a commercial hydrophobic coating transformed from hydrophobicity to hydrophilicity. This result implied our superhydrophobic surface coating was very stable. Moreover, chalk powders on the superhydrophobic surface coatings could easily be washed off with water, indicating good self-cleaning properties. The presented approach is convenient and can be potentially applied in fabrication of superhydrophobic surfaces in large scale.

Preparation of Superhydrophobic PMHS-SiO_2 Coatings by Sol-Gel Method

Formation of AlOOH and Silica Composite Hierarchical Nanostructures Thin Film by Sol–gel Dip-Coating for Superhydrophobic Surface with High Adhesion Force

Percolation-dominated Superhydrophobicity and Conductivity for Nanocomposite Coatings from the Mixtures of a Commercial Aqueous Silica Sol and Functionalized Carbon Nanotubes

Preparation and Research of Hydrophobic PDMS/Nano-SiO2 Modified SiO2 Coating

The preparation and properties research of superhydrophobic organosilicone coating

Fabrication of PMMA Superhydrophobic Surface Coating by Hot Embossing/Spray Method

In Situ Preparation of Recoverable Superhydrophobic Coatings for Various Environments

Preparation and Properties of Superhydrophobic Fluoroalkylsilane Coatings

Facile Fabrication and Antifogging Test of a Calcination-Free SiO_2 Superhydrophilic Coating

A robust, room-temperature curable and molecular-level superhydrophobic coating with excellent antibacterial and antifouling properties

Preparation and Effect Factors of TiO2 Superhydrophobic Coating

Preparation of a temperature-sensitive superhydrophobic self-cleaning SiO2-TiO2@PDMS coating with photocatalytic activity

Heat Stability and Icing Delay on Superhydrophobic Coatings in Facile One Step

Preparation and Characterization of Super-Hydrophobic Silica Coating by HVOF

Fabrication of silicone modified polyurethane matrix superhydrophobic coating with hydroxy-terminated polydimethylsiloxane modified SiO2 nanoparticles

Fabrication of superhydrophobic transparent coatings prepared by spraying dual-sized silica particles

Fabrication of Superhydrophobic Coating Based on Waterborne Silicone-Modified Polyurethane Dispersion and Silica Nanoparticles

Fabricating Superhydrophobic and Oleophobic Surface with Silica Nanoparticles Modified by Silanes and Environment-Friendly Fluorinated Chemicals

PREPARATION AND PROPERTIES OF SUPERHYDROPHOBIC POLYPHENYLENE SULFIDE COMPOSITE COATINGS

Preparation of a wear-resistant, superhydrophobic SiO2/silicone-modified polyurethane composite coating through a two-step spraying method

Preparation and Thermal Stability of Polyorganosiloxane Superhydrophobic Film by Sol-Gel Method