Abstract:Generally, superhydrophilic self-cleaning coatings are prepared from semiconductors with photocatalytic properties. Organic pollutants attached to the coating surface can be degraded by its photocatalytic performance realizing a self-cleaning goal. Herein, SiO2–TiO2 composite particles were fabricated by the hydrolysis and precipitation of TiOSO4, and SiO2 microspheres were chosen as carriers, which are inexpensive and environmentally friendly. Then, superhydrophilic self-cleaning SiO2–TiO2 coatings were fabricated by spraying the composites on the surfaces of substrates. The morphology, structure and self-cleaning performance of the SiO2–TiO2 coating were characterized and tested. The results revealed that nano-TiO2 was loaded on the surfaces of SiO2 microspheres uniformly forming a hierarchical micro/nanostructure. The SiO2–TiO2 composite particles exhibited excellent photocatalytic degradation performance, and the degradation rate of methyl orange (10 ppm) was more than 98% under UV irradiation for 40 min. Furthermore, the coating prepared with the SiO2–TiO2 composite particles exhibited superhydrophilicity. A water droplet spreads completely on the coating surface in 0.35 s, and the contact angle reaches 0°. In addition, rhodamine B (RhB) and methylene blue (MB) on the coating surface can be degraded efficiently under sunlight irradiation. The SiO2–TiO2 composite particles can be sprayed directly on the surfaces of concrete, brick, wood, and glass slides. Therefore, the particles showed good adaptability to different substrates. The superhydrophilic property was due to the hydrophilicity of SiO2 and TiO2, the hierarchical micro/nanostructure of the SiO2–TiO2 composites, and the photoinduced superhydrophilicity of TiO2. The above experimental results show that the as-prepared superhydrophilic self-cleaning SiO2–TiO2 coating has a large application potential.

Preparation and characterization of SiO2–TiO2 superhydrophilic coatings with photocatalytic activity induced by low temperature

Fabrication of Modifier-Free Superhydrophobic Surfaces with Anti-Icing and Self-Cleaning Properties on Ti Substrate by Anodization Method

Preparation of a temperature-sensitive superhydrophobic self-cleaning SiO2-TiO2@PDMS coating with photocatalytic activity

Fabrication of superhydrophilic self-cleaning SiO2–TiO2 coating and its photocatalytic performance

The preparation of superhydrophobic photocatalytic fluorosilicone/SiO2–TiO2 coating and its self-cleaning performance

Facile Fabrication and Antifogging Test of a Calcination-Free SiO_2 Superhydrophilic Coating

Study of Self-Cleaning and Low-Emission Properties of FTO/TiO2 Composite films

Preparation of Superhydrophobic PMHS-SiO_2 Coatings by Sol-Gel Method

Study on the Superhydrophilicity of the SiO2-TiO2 Thin Films Prepared by Sol-Gel Method at Room Temperature

Preparation and characterization of superhydrophilic self-cleaning coating for solar cell cover glass applications

Preparation and Effect Factors of TiO2 Superhydrophobic Coating

Preparation of TiO2 Thin Films at Low Temperature and Characterization of Their Properties

Preparation of TiO2/SiO2 Composite by Chemical Coating Method

Tunable Adhesive Self-Cleaning Coating with Superhydrophobicity and Photocatalytic Activity

Heat Stability and Icing Delay on Superhydrophobic Coatings in Facile One Step

Super-Hydrophilic TiO2/SiO2 Composite Thin Films Prepared by RF Magnetron Co-Sputtering

Superhydrophobic and photothermal SiC/TiN durable composite coatings for passive anti-icing/active de-icing and de-frosting

Preparation and characterization of Superhydrophilic TiO2-SiO2 films for double-layer broadband antireflective coating

Preparation and Characterization of Super-Hydrophobic Surface Through Particle Deposition by Vacuum Cold Spray

Preparation of SiO2 resin coating with superhydrophobic wettability and anti-icing behavior analysis

Self-healing superhydrophobic A-SiO2/N-TiO2@HDTMS coating with self-cleaning property