Super high-pressure moulding of Fe86Zr5Nb6B3 amorphous alloy

Bin Lü,Danqing Yi,Biao Yan,JunLin Yin,Huiqun Liu,Biaoli Wu,Xiaoli Chen
DOI: https://doi.org/10.3321/j.issn:1002-185x.2006.01.020
2006-01-01
Rare Metal Materials and Engineering
Abstract:The thermal stability of ball milling powder of Fe86Zr5Nb6B3 melt-spinning strip and the influence of high-pressure sintering conditions on phase components and grain size of bulk alloy were investigated by XRD, DSC and TEM. The results show that: (1) after ball milling melt-spinning powders are still amorphous, crystallization temperature of which is about 510 degrees C. The apparent activation energy of this crystallization process is E=219.5 W/mol; (2) under P=5.5 GPa, 3 min sintering conditions, when P-w=1150 W, single phase a-Fe nanocrystalline (20.6 nm) bulk alloy with 99.1% relative density can be obtained; (3) under 5.5 GPa, 1150 W sintering conditions, when t=25 min the grain size of a-Fe phase increase to 28.7 nm; (4) under 5.5 GPa, 1150W, 5 min sintering conditions, the saturate magnetization B-s and coercive force H-c of as-required nanocrystalline bulk alloy is 1.26 T and 4.27 kA(.)m(-1), respectively.
What problem does this paper attempt to address?