Abstract:ZnO hexagonal sub-microrods have been synthesized onto glass substrates through aqueous growth method by using the thermal decomposition of an aqueous solution of equimolar zinc nitrate(Zn(NO_3)_2·4H_2O) or zinc acetate(Zn(CH_3COO)_2·2H_2O))with methenamine ((CH_2)_6N_4) by controlling the experimental conditions. XRD patterns, SEM images have been measured, which reveals the shape of the most of the ZnO sub-microrods are hexagonal-rod with two flat faces on the two ends, but some are pair rods symmetrically grown from a center to both sides and some form radial clusters from one center. The length of the rods is from 5 μm to 8 μm, the diameter from 300 nm to 700 nm and the ratio of the length to the diameter is more than 10∶1. When the growth time reaches 48 h, we found that the microrods turned into hollow microtubes with the tube-thickness in the tenth of diameter. The growth mechanism is discussed by using the growth model of cathodion ligand tetrahedron. Zn-(NO_3)_2 dissolves and forms growth units of tetrahedron Zn-(OH)_4 under the reaction of the surface activator (CH_2)_6N_4. Then the incorporation of growth units leads to the formation of the ZnO crystal lattice at the interface through a dehydration reaction (OH~-+ OH~-H_2O+O~ 2- ). The fastest of the growth speed along 0001- direction leads to the formation of the ZnO microrods. The reason of forming hollow microtubes is the face of (0001) and 0001- of ZnO rods as eroded by chemical dissolution because of its metastable state. The excitation spectra of ZnO sub-microrods show that except the intrinsic inter-band excitation shorter than 370 nm, there is a strong exciton excitation peak located at around 377~385 nm at room temperature. The photoluminescent spectra show that there is a wide orange-red emission peaking at about 630 nm and FWHM 250 nm with the excitation wavelength 310 nm. When the excitation is a strong 325 nm He-Cd laser, the same sample will emit a strong excition emission peaking at about 385 nm, with FWHM 16 nm and a green emission peaking at about 552 nm with FWHM 120 nm. Compared with the calculated data of these intrinsic defects with the theory of FP-LMTO, the green, orange-red and red emission peaks can be attributed to the transition of oxygen vacancies to the valence band. The studies on PL of ZnO sub-microrods after annealing showed that the excitation peak at about 384 nm disappeared, and the orange-red defect emission (peak at ~630 nm) shows red shift (peak at ~710 nm), and the emission intensity increases. The excitation spectra of samples after annealing showed an enhanced exciton peak at ~377 nm. It indicates that after annealing, the energy transfer from the excition to the defect center occurred.

Synthesis and photoluminescence of Eu-doped ZnO microrods prepared by hydrothermal method

Synthesis and Photoluminescence Properties of Self‐assembled Eu‐doped ZnO Hollow Microspheres

Structure, X-ray photoelectron spectroscopy and photoluminescence properties of highly ordered ZnO microrods

Correlation of luminescent properties of ZnO and Eu doped ZnO nanorods

ZnO:Eu thin-films: Sol–gel derivation and strong photoluminescence from 5D0→7F0 transition of Eu3+ ions

Low temperature chemical reaction synthesis of single-crystalline Eu(OH)<sub>3</sub> nanorods and their thermal conversion to Eu<sub>2</sub>O<sub>3</sub> nanorods

Preparation and Photoluminescence of ZnO with Nanostructure by Hollow-Cathode Discharge

Hydrothermal Synthesis and Photoluminescent Properties of ZnO Nanorods

Photoluminescence and ZnO → Eu3+energy Transfer in Eu3+-doped ZnO Nanospheres

Hydrothermal synthesis, controlled microstructure, and photoluminescence of hydrated Zn<sub>3</sub>(PO<sub>4</sub>)<sub>2</sub>: Eu<sup>3+</sup> nanorods and nanoparticles

Photoluminescence and Raman Scattering of ZnO Nanorods

Crystal Growth and Luminescent Properties of ZnO Sub-microrods Prepared by One Step Solution Growth Method

Crystal Growth and Luminescent Properties of ZnO Sub-microrods and Microrods

Preparation, photoluminescence and photocatalytic properties of ZnO:Eu3+ nanocrystals

Synthesis, Characterization and Photoluminescence of Y_2O_3:Eu~(3+) Nanorods by the Combination of Microemulsion and Microwave Heating

Hydrothermal synthesis, controlled microstructure, and photoluminescence of hydrated Zn 3 (PO 4 ) 2 : Eu 3+ nanorods and nanoparticles

Hydrothermal synthesis, controlled microstructure, and photoluminescence of hydrated Zn(PO): Eu nanorods and nanoparticles

Synthesis and Optical Characterizations of ZnO Nanorods

Synthesis and Photoluminescent Properties of Wurtzite Zns Nanorods by Hydrothermal and Co-Precipitation Methods

Preparation and luminescence property of ZnWo4:Er3+, Yb3+ nanorods

Hydrothermal Preparation and Photoluminescence Property of Co-Doped ZnO Nanorods