Abstract:ZnO hexagonal sub-microrods have been synthesized onto glass substrates through aqueous growth method by using the thermal decomposition of an aqueous solution of equimolar zinc nitrate(Zn(NO_3)_2·4H_2O) or zinc acetate(Zn(CH_3COO)_2·2H_2O))with methenamine ((CH_2)_6N_4) by controlling the experimental conditions. XRD patterns, SEM images have been measured, which reveals the shape of the most of the ZnO sub-microrods are hexagonal-rod with two flat faces on the two ends, but some are pair rods symmetrically grown from a center to both sides and some form radial clusters from one center. The length of the rods is from 5 μm to 8 μm, the diameter from 300 nm to 700 nm and the ratio of the length to the diameter is more than 10∶1. When the growth time reaches 48 h, we found that the microrods turned into hollow microtubes with the tube-thickness in the tenth of diameter. The growth mechanism is discussed by using the growth model of cathodion ligand tetrahedron. Zn-(NO_3)_2 dissolves and forms growth units of tetrahedron Zn-(OH)_4 under the reaction of the surface activator (CH_2)_6N_4. Then the incorporation of growth units leads to the formation of the ZnO crystal lattice at the interface through a dehydration reaction (OH~-+ OH~-H_2O+O~ 2- ). The fastest of the growth speed along 0001- direction leads to the formation of the ZnO microrods. The reason of forming hollow microtubes is the face of (0001) and 0001- of ZnO rods as eroded by chemical dissolution because of its metastable state. The excitation spectra of ZnO sub-microrods show that except the intrinsic inter-band excitation shorter than 370 nm, there is a strong exciton excitation peak located at around 377~385 nm at room temperature. The photoluminescent spectra show that there is a wide orange-red emission peaking at about 630 nm and FWHM 250 nm with the excitation wavelength 310 nm. When the excitation is a strong 325 nm He-Cd laser, the same sample will emit a strong excition emission peaking at about 385 nm, with FWHM 16 nm and a green emission peaking at about 552 nm with FWHM 120 nm. Compared with the calculated data of these intrinsic defects with the theory of FP-LMTO, the green, orange-red and red emission peaks can be attributed to the transition of oxygen vacancies to the valence band. The studies on PL of ZnO sub-microrods after annealing showed that the excitation peak at about 384 nm disappeared, and the orange-red defect emission (peak at ~630 nm) shows red shift (peak at ~710 nm), and the emission intensity increases. The excitation spectra of samples after annealing showed an enhanced exciton peak at ~377 nm. It indicates that after annealing, the energy transfer from the excition to the defect center occurred.

Structure, X-ray photoelectron spectroscopy and photoluminescence properties of highly ordered ZnO microrods

Growth Mechanism And Properties Of Zno Nanorods Synthesized By Plasma-Enhanced Chemical Vapor Deposition

Crystal Growth and Luminescent Properties of ZnO Sub-microrods and Microrods

Crystal Growth and Luminescent Properties of ZnO Sub-microrods Prepared by One Step Solution Growth Method

Photoluminescence and Raman Scattering of ZnO Nanorods

Fabrication and Optical Character of High Quality ZnO Microrods

Structure evolution and optical properties of hierarchical ZnO micro/nanorods fabricated by a two-step growth method

Preparation and Photoluminescence of ZnO with Nanostructure by Hollow-Cathode Discharge

Synthesis and Characteristics of Large-Scale ZnO Rods by Wet Chemical Method

Photoluminescence and Field Emission of 1D ZnO Nanorods Fabricated by Thermal Evaporation

Photoluminescence and Raman analysis of ZnO microwires synthesized by chemical vapour deposition

Synthesis and Optical Characterizations of ZnO Nanorods

Structural And Luminescent Properties Of Zno Nanorods Prepared From Aqueous Solution

The Structure and Photoluminescence Properties of ZnO Nanobelts Prepared by a Thermal Evaporation Process

Microwave Assisted Hydrothermal Synthesis of Hierarchical Structured ZnO Nanorods

Photoluminescence Characterization of Nanocrystalline ZnO Array

Zinc Oxide Nanorods Grown by Arc Discharge

X-ray Absorption and Emission Spectroscopy of ZnO Nanoparticle and Highly Oriented ZnO Microrod Arrays

Synthesis, optical and field electron emission properties of low-dimensional ZnO nano-structures

Synthesis and optical properties of single crystal ZnO nanorods

Structural and Luminescent Properties of ZnO Nanorods and ZnO/ZnS Nanocomposites