Abstract:ZnO nanowires were successfully fabricated by using the hydrothermal method in the existence of the poly ethylene glycol (PEG) with the molecular weight of 200. The experimental results exhibit that the ZnO nanowires with the diameter of ~30nm and the length of ten micrometers. PL spectra show a weak ultraviolet emission and an intense broad visible emission band for as-grown and annealed samples. These visible emission bands exhibit red-shifts from green (545nm) to yellow (580nm) and blue-shifts from yellow (580nm) to green (520nm) by annealing at aerobic or anaerobic environment, it indicates that the defect types are changed by annealed at different environment. Additionally, the red-shifts (520nm) and blue-shifts (580) can match up the bimodal lorentzian fitting (520nm and 583nm) of as-growth, which suggest that the visible emission band (545nm) is closely related to oxygen defects. The oxygen atomic can enter into the crystal lattice of ZnO and decrease the oxygen vacancy in air or oxygen, whereas, more oxygen vacancy defects is gave rise in vacuum annealed. We guess the energy levels of the intrinsic defects in ZnO nanowire maybe like that: the electrons of Zni defects compound with holes of VZn, Oi and OZn levels and conform to the yellow emission, and the green emission corresponds to the electron transition from the association defects deep donor level to the valence band.

Hydrothermal Synthesis and Photoluminescent Properties of ZnO Nanorods

Synthetic and Effect of Annealing on the Luminescent Properties of Zno Nanowire

Facile synthesis of Zn 1−x Cu x O nanorods with a very broad visible band

Hydrothermal Preparation and Photoluminescence Property of Co-Doped ZnO Nanorods

Low Temperature Synthesis and Optical Properties of Small-Diameter ZnO Nanorods

Temperature-Dependent Photoluminescence of Zno Nanorods Prepared by A Simple Solution Route

A Simple and Novel Low-Temperature Hydrothermal Synthesis of ZnO Nanorods

Preparation and photoluminescence of ZnO nanorods

Preparation and Photoluminescence of ZnO with Nanostructure by Hollow-Cathode Discharge

Hydrothermal Synthesis and Optical Properties of ZnO Nanostructured Films Directly Grown From/on Zinc Substrates

Hydrothermal self-assembling of ZnO nanorods into sphere-like superstructures and their optical characteristics

Hydrothermal Synthesis of Well-Aligned ZnO Nanorod Arrays on Silicon

Photoluminescence Properties of Co-doped ZnO Nanorods Array Fabricated by the Solution Method

Full-color Photoluminescence of ZnO Nanorod Arrays Based on Annealing Processes

Cathodoluminescence and its mapping of flower-like ZnO, ZnO/ZnS core–shell and tube-like ZnS nanostructures

Preparation, photoluminescence and photocatalytic properties of ZnO:Eu3+ nanocrystals

Structural and Luminescent Properties of ZnO Nanorods and ZnO/ZnS Nanocomposites

Temperature-Dependent Photoluminescence of Nanostructured ZnO

Dominant Free Exciton Emission in ZnO Nanorods

PEG Assisted Hydrothermal Synthesis of ZnO Nanorods

Hydrothermal Synthesis and Gas Sensing Characters of Zno Nanorods