Effects of pH value and calcining temperature on indium tin oxide nanopowder synthesized by co-precipitation
Yu-lu DUAN,Rui YE,Xing-chen YAN,Cheng DAI,Jiang TAN,Guo-fu XU
DOI: https://doi.org/10.3969/j.issn.1673-0224.2014.03.013
2014-01-01
Abstract:The Sn-doped In2O3(ITO) nanopowders were preparated by chemical co-precipitation with 99.99% In and SnCl4·5H2O as raw materials. The ITO precursor was analyzed by TG-DSC, and the morphology characterization, phase composition and particle size of the ITO nanopowders were characterized by XRD, SEM, TEM, BET and XPS. The effects of pH value of the reaction end and calcining temperature on the phase composition, the morphology characterization and particle size of the ITO nanopowders were investigated. The results show that the ITO nanopowders are synthesized under the conditions of adding sodium silicate in the liquid phase, reaction temperature of 60 ℃, the reaction end point at pH=8, the aging time for 60 min, and calcined system for 2 h and 750 ℃, the obtained ITO nanopowder is In2O3 solid solution with a cubic structure, which is the single structure without SnO2 phase. And the ITO powders are of high purity, uniform particle size, and good dispersibility, which is nearly spherical. The particle size of the ITO nanopowders is in the range of 30~60 nm, and the specific surface area of powders is about 34.26 m2/g.