Susceptibility to Welding Cold Cracking of 30Crmnsini2a

NIU Jing,DONG Jun-ming,DONG Wei-peng,HE Yuan,XUE Jin

DOI: https://doi.org/10.3969/j.issn.1000-3738.2006.07.007

2006-01-01

Abstract:Implant test equipment was used to measure critical fracture stresses of the fusion area under different conditions.Microstructure of the joints and fracture morphology of implant samples were analyzed.The zone of the most susceptibility to cold cracking was the fusion area in implant welding joints.The fracture morphology of the fusion area was in intergranuar form with a few quasicleavage.The microstructure of the fusion area was a combination of martensite,bainite and retained austenite.The hydrogen content of HTJ-3 electrode was more than that of HTG-1 electrode,so the critical fracture stress of the former fusion area was less than that of the latter.Stress distribution in implant welding joint were affected by the notch.