Abstract:The effect of lanthanum (La) content on the phase transformation of Pb1-3x/2Lax(Zr0.42Sn0.40Ti0.18)O-3 (PLZST 100x/42/40/18, 0x0.06) ceramics was investigated by the dielectric and ferroelectric properties. The base composition PLZST 0/42/40/18 located in the ferroelectric (FE) rhombohedral phase region. As x increased, the compositions showed successively FE and antiferroelectric (AFE) state at room temperature, and their peak temperatures (T-max) decreased gradually in line as T-max=162.21-1507x. Evidence was presented that there were two dielectric anomalies in PLZST 2/42/40/18, which were corresponding to the FE-AFE and AFE-paraelectric (PE) phase transformations, respectively. With increasing the dc bias fields, the two phases merged into one. PLZST 3/42/40/18 showed AFE characteristics with the first loop outside of the second loop and there was only one dielectric inflection. The critical lanthanum content occurred at x=0.03 from the dielectric temperature spectra and hysteresis loops. Furthermore increase in La above 0.03, these compositions showed typical antiferroelectric behaviors with double hysteresis loops. The stored energy properties of the three compositions (PLZST 4/42/40/18, 5/42/40/18 and 6/42/40/18) displayed different temperature dependencies from room temperature to 140 degrees C (over their respective T-max). Comparing the above results with previous investigations on PLZSTs, some questions were discussed.

Synthesis, Sintering and Characterization of PLZST Perovskite Prepared by a Lactate Precursor Route

Preparation of Plzst with Complex Perovskite Structure by Coprecipitation

Study on Chemical Fabrication of Lead Zirconate Stannate Titanate (plzst) Doped with Rare Earth Element Lanthanum

Microstructure and dielectric properties of PLZST ceramics prepared by a modified coprecipitation

Preparation of Lead Lanthanum Zirconate Stannate Titanate Antiferroelectric Ceramics by Modified Coprecipitation Method

Molten Salt Synthesis of Lead Lanthanum Zirconate Titanate Stannate Powders and Ceramics

Low temperature synthesis of (Pb,La)(Zr,Sn,Ti)O 3 powders by citrate process

Synthesis of Pb(Zr0.52Ti0.48)O3(PZT) Powder by A Partial Lead Oxalate Coprecipitation Method

Effect of Zr:Sn ratio in the lead lanthanum zirconate stannate titanate ceramics on microstructure and electric properties

Preparation of PLZT Powders from Oxides Via High-Energy Ball Milling Process

Effects of Preparation Conditions on the Structural and Optical Properties of Spark Plasma‐Sintered PLZT (8/65/35) Ceramics

Pva Assisted Synthesis of Nanosized Perovskite Pzt Powder by A Two-Stage Precipitation Route

Synthesis of PbZrO3 Powder by a COprecipitation Method

Effect of A-site La3+ Modified on Dielectric and Energy Storage Properties in Lead Zironate Stannate Titanate Ceramics

Effect of KOH Concentration on the Phase and Morphology of Hydrothermally Synthesized Pb0.70La0.30TiO3 Fine Powders

Effect of La-Introduced Manner on the Phase Formation and Morphology of the Hydrothermally Synthesized Pb_(0.70)La_(0.30)TiO_3 Powders

Dielectric and Ferroelectric Properties of Lanthanum‐modified Lead Zirconate Stannate Titanate (42/40/18) Ceramics

Processing and characterization of lead zirconate titanate nanopowders by a simple water-based sol-gel method

Preparation of lead lanthanum zirconate titanate stannate ceramics by partial chemical method and its electric field induced strain properties

Hydrothermally synthesized Pb0.70La0.30TiO3 powders

Synthesis Of Perovskite Pb(Zr0.52ti0.48)O-3 (Pzt) Powders By A Modified Coprecipitation Method