Abstract:The effect of nitrogen content on the formation of an equiaxed solidification structure of Fe-16Cr steel was investigated. Moreover, two different kinds of refractory materials, i.e., alumina and magnesia, were employed to control the type of oxide inclusion. The characteristics of TiN(-oxide) inclusions were quantitatively analyzed in both molten steel and solidified samples. When the melting was carried out in the alumina refractory, the grain size continuously decreased with increasing nitrogen content. However, a minimum grain size was observed at a specific nitrogen content (approx. 150 ppm) when the steel was melted in the magnesia refractory. Most of the single TiN particles had a cuboidal shape and fine irregularly shaped particles were located along the grain boundary due to the microsegregation of Ti at the grain boundary during solidification. The type of TiN-oxide hybrid inclusion was strongly affected by the refractory material where Al2O3-TiN and MgAl2O4-TiN hybrid-type inclusions were obtained in the alumina and magnesia refractory experiments, respectively. The formation of oxide inclusions was well predicted by thermochemical computations and it was commonly found that oxide particles were initially formed, followed by the nucleation and growth of TiN. When the nitrogen content increased, the number density of TiN linearly increased in the alumina refractory experiments. However, the number of TiN exhibits a maximum at about [N] = 150 ppm, at which a minimum grain size was obtained in the magnesia refractory experiments. Therefore, the larger the number density of TiN, the smaller the primary grain size after solidification. The number density of TiN in the steel melted in the magnesia refractory was greater than that in the steel melted in the alumina refractory at given Ti and N contents, which was due to the lower planar lattice disregistry of MgAl2O4-TiN interface rather than that of Al2O3-TiN interface. When ∆TTiN (= difference between the TiN precipitation temperature and the liquidus of the steel) was 20 K to 40 K, the number density of effective TiN was maximized and thus, the grain size was minimized after solidification. Finally, although most of the TiN particles were smaller than 1 μm in the molten steel samples irrespective of the nitrogen content, TiN particles larger than 10 μm were observed in the solidified samples when the nitrogen content was greater than 150 ppm. The growth of TiN particles during melting and solidification was well predicted by the combinatorial simulation of the ‘Ostwald ripening model’ based on the Lifshitz–Slyozov–Wagner theory in conjunction with the ‘Diffusion controlled model’ using Ohnaka’s microsegregation equation.

THE REFINING EFFECT OF Fe-Ti-N NUCLEATION ALLOY ON THE SOLIDIFIED STRUCTURE OF INDUSTRIAL PURE IRON

Solidification structure refining of 409L ferritic stainless steel using Fe-Ti-N master alloy

Synergistic Effect of Nitrogen and Refractory Material on TiN Formation and Equiaxed Grain Structure of Ferritic Stainless Steel

Grain Refining of 409L Ferritic Stainless Steel Using Fe-Ti-N Master Alloy

Fe nanoparticles modified pure Ti alloy on microstructure evolution and fine crystallization mechanism fabricated by additive manufacturing

Influence of Fe on grain nucleation and growth of pure aluminum during refining by Al-Ti-B and Al-Ti-C master alloys

Effect of Microstructure Before Nitrogenation on Magnetic Properties of SmFeN Alloys

Effect of Mg–Ti Treatment on Nucleation Mechanism of TiN Inclusions and Ferrite

Effect of Fe on Grain Refining of Pure Aluminum Refined by Al5tib Master Alloy

In-situ Synthesis of TiN and its Effects on Fe-12Cr-6Al in Laser Powder Bed Fusion

Refinement of Intermetallic Compounds of Zn-2Ni Alloy

Refining mechanism for TiN and solidification structure through a nucleating chain in magnesium-yttrium-treated ultrapure ferritic stainless steel

In-situ Observations of Grain Refinement by TiN Particles in the Simulated Coarse-Grained Heat-Affected Zone of a High-Strength Low-Alloy Steel

Solidification Structure Formation in Undercooled Fe–Ni Alloy

Study on Grain Refinement of A357 Alloy Using Al-5Ti-1B

Effect of TiO2 Particle Size on Microstructure and Refining Effect of Al-TiO2-C Refiner

Refining Effect of Aluminum-Rare Earths on Structure of Zn-2%Ni Alloy

Control of TiN precipitation behavior in titanium-containing micro-alloyed steel

Effect of In-Situ Nanoparticles Induced by Ti Addition on the Microstructure and Tribological Properties of FeCrB Alloys

Refinement Effectiveness of Self-Prepared (nbti)c Nanoparticles on As-Cast 1045 Steel

The Evaluating Study of the Refining Effect of Al-Ti-C and Al-Ti-B on Aluminum