A Novel Al-Ti-C-B-Ce Alloy Preparation Process and Its Refinement Effect to A356 Alloy
Tong Liu,Maoliang Hu,Qingyu Ran,Bo Jiang,Zesheng Ji,Xiaobing Zhou
DOI: https://doi.org/10.1007/s11837-023-06258-8
2023-11-14
JOM
Abstract:A novel Al-5Ti-0.2C-0.2B-1Ce aluminum alloy refining agent was prepared in this study by using Al and Ti-6Al-4 V chips as the main materials generated during a machining process. The analysis results showed that the second phase of the refiner was mainly composed of TiAl 3 , Ti 2 Al 20 Ce, TiC, and TiB 2 . Among them, the V, B, and C elements were doped between TiC and TiB 2 to form TiC-B-V and TiB 2 -C-V particles. We explored the optimal preparation process of this refiner and the variation law of the included second phase with temperature and time. In Al-5Ti-0.2C-0.2B-1Ce prepared at 1000°C and refined for 60 min, the pure aluminum grain size reduced from 4187.6 μm to 296.7 μm with the addition of 0.3 wt.%. This kind of refining agent also has a certain resistance to Si poisoning, which effectively refines the grain size of the A356 alloy from 88.9 μm to 38.1 μm, an increase of 15.4% in its tensile strength.
materials science, multidisciplinary,metallurgy & metallurgical engineering,mining & mineral processing,mineralogy