EFFECT OF MIGRATORY CORROSION INHIBITORS ON THE DURABILITY OF CHLORIDE-CONTAMINATED REREINFORCED CONCRETE——ELECTROCHEMICAL PERFORMANCE AND PENETRATION CONCENTRATION

刘志勇,缪昌文,孙伟

DOI: https://doi.org/10.3321/j.issn:0454-5648.2009.07.035

2009-01-01

Abstract:Corrosion of the steel bars in concrete is the major cause of premature deterioration of reinforced concrete structures. To improve the durability and extend the service life of concrete structures under chloride condition, various methods (such as adding admixture, using high performance concrete and epoxy coated steel bar) have been used. In the existing techniques available, the mi-gration of corrosion inhihitors (MCIs) used as admixtures shows a versatility in the surface treatments and in rehabilitation. The in-hibiting effectiveness and the migratory performance of amino alcohol (AMA) and amine carboxylate for the MCIs in chloride con-taminated concrete were investigated. The harden reinforced concrete specimens(C30) contaminated with 0.5% NaCI by mass of the cementitions materials in the mixing process were experienced by a adequate curing and were subjected to two-month exposure tests after painting with 400 g/m2 of the MCIs. The corrosion behavior of the steel bat in specimens was monitored using electrochemical impedance spectroscopy (EIS), open circuit potential, linear polarization resistance (LPR) and corrosion currents. The results show that the steel bars in concrete samples after surface painting the MCIs for 60d give a lower corrosion current of 0.104 μA/cm2, com-pared to the untreated sample (3.77 μA/cm2). The minimum corrosion current of the sample coated with #6 inhibitor could be reduced to 1.1% of the untreated sample. The nitrogen concentration depth profiles for concrete samples treated with the MCIs were analyzed. The higher organic nitrogen content in the depth of 30-40 mm indicates that the inhibitors assuredly migrate through the concrete capillary and micro-crack to the steel bars in cover concrete. The results show that the MCIs are effective in the suppression of the corrosion development or the rehabilitation of the corrosive steel bar when they are applied on the surface of the hardened concrete even though the initiation of corrosion in the presence of chloride.