Abstract:The migratory performance of surface applied amino alcohol and amine carboxylate based migrating corrosion inhibitors(MCIs) on the reinforced concrete and the inhibiting effectiveness on the steel bar beneath the cover of concrete adding 0.5% NaCl by mass of the cementious materials in mixing were investigated.The corrosion behavior of steel bar in the samples before and after painting the MCIs had been determined by electrochemical impedance spectroscopy,linear polarization resistance and corrosion currents for seven months.The results show that the reinforcements in concrete samples(No.1-No.8) after painting the MCIs for 7 months give an average corrosion rate of 0.136 μA/cm2,which is approximately 3.6% of the samples' average current before painting inhibitors(3.766 μA/cm2).Excluding the impact of enhancement of concrete resistance on the current with the extension of age,it was estimated that the average corrosion current of the painted samples with the MCIs is approximately 16% of the current of unpainted sample at the same age using the unpainted sample as a reference.Among the 8 kinds of MCIs,the inhibition performance of amine carboxylates-based inhibitors(No.3-No.7) and the commercial MCI(No.8) was superior.A higher nitrogen content in cover depths of 30-40 mm can explained the migration of inhibitors onto the rebar surface through the concrete capillary and micro-crack after painting MCIs for 7 months.The analysis showes the presence of inhibitors on the steel bar surface.In addition,the corresponding mechanism is also discussed.

EFFECT OF MIGRATORY CORROSION INHIBITORS ON THE DURABILITY OF CHLORIDE-CONTAMINATED REREINFORCED CONCRETE(Ⅱ)-LONG-TERM EFFECT, MORPHOLOGICAL AND MECHANISMIC ANALYSIS