Abstract:As a toxic pollutant, carbon monoxide (CO) usually causes harmful effects on human health. Therefore, the thermally catalytic oxidation of CO has received extensive attention in recent years. The CuO-based catalysts have been widely investigated due to their availability. In this study, a series of transition metal oxides (Fe2O3, Co3O4 and NiO) promoted CuO-based catalysts supported on the α-MnO2 nanowire catalysts were prepared by the deposition precipitation method for catalytic CO oxidation reactions. The effects of the loaded transition metal type, the loading amount, and the calcination temperature on the catalytic performances were systematically investigated. Further catalyst characterization showed that the CuO/α-MnO2 catalyst modified with 3 wt% Co3O4 and calcined at 400 °C performed the highest CO catalytic activity (T90 = 75 °C) among the investigated catalysts. It was supposed that the loading of the Co3O4 dopant not only increased the content of oxygen vacancies in the catalyst but also increased the specific surface area and pore volume of the CuO/α-MnO2 nanowire catalyst, which would further enhance the catalytic activity. The CuO/α-MnO2 catalyst modified with 3 wt% NiO and calcined at 400 °C exhibited the highest surface adsorbed oxygen content and the best normalized reaction rate, but the specific surface area limited its activity. Therefore, the appropriate loading of the Co3O4 modifier could greatly enhance the activity of CuO/α-MnO2. This research could provide a reference method for constructing efficient low-temperature CO oxidation catalysts.

Low-Temperature Catalytic Reduction of Nitrogen Monoxide with Carbon Monoxide on Copper Iron and Copper Cobalt Composite Oxides

Catalytic Reduction of NO by NH3 over Fe–Cu–OX/CNTs-TiO2 Composites at Low Temperature

Low-Temperature Co Oxidation Over Cuo/Co3o4 Catalysts

Low-temperature CO Oxidation over CuO/Fe2O3 Catalysts

Activation of Fast Selective Catalytic Reduction of NO by NH3 at Low Temperature over TiO2 Modified CuOX-CeOX Composites

Treatment Induced Remarkable Enhancement of Low-Temperature Activity and Selectivity of Copper-Based Catalysts for No Reduction

Characterization and Catalytic Activity of Mn-Co/TiO2 Catalysts for NO Oxidation to NO2 at Low Temperature

Peanut-Shaped Cu–Mn Nano-Hollow Spinel with Oxygen Vacancies as Catalysts for Low-Temperature NO Reduction by CO

Synergy Between FeOX and CuOX in FeCuOX/TiO2-hBN Composites for NO Reduction with NH3

Nickel foam supported CuCe mixed metal oxide as monolith catalyst for NO removal

Investigation of Fe-Ni Mixed-Oxide Catalysts for the Reduction of NO by CO: Physicochemical Properties and Catalytic Performance

Low temperature selective catalytic reduction of NOx by NH3 over Cu modified V2O5/TiO2–carbon nanotube catalyst

Selective reduction of NO by CO using copper-aluminum oxides from hydrotalcite-type precursors: Study of chemical species and thermal stability

Enhanced Low-Temperature CO-SCR Denitration Performance and Mechanism of Two-Dimensional CuCoAl Layered Double Oxide

Study on Catalytic Reduction of NO on CuO/TiZrO4 in the Presence of Excess Oxygen

Transition Metal (fe2o3, Co3O4 and NiO)-Promoted CuO-Based Α-Mno2 Nanowire Catalysts for Low-Temperature CO Oxidation

Hierarchically interconnected porous Mn Co3-O4 spinels for Low-temperature catalytic reduction of NO by CO

Insights into the highly activity CuMgFe oxides for the selective catalytic reduction of NO by CO: Structure-activity relationships and K/SO2 poisoning mechanism

DRIFT Study of CuO-CeO₂-TiO₂ Mixed Oxides for NOx Reduction with NH₃ at Low Temperatures.

CeO2 nanoparticles modified by CuO nanoparticles for low-temperature CO oxidation with high catalytic activity

Assessment of copper-iron catalyst supported on activated carbon for low-temperature nitric oxide reduction by hydrogen