Abstract:The composite T-joint, a typical structural element, is widely used in the fields of aerospace due to their excellent mechanical properties. However, several defects might occur in this material during manufacturing because of the application of co-curing and co-bonding technologies. The existence of the defects results in the reduction in the load bearing capacity, which negatively affects the safety of the structure. In this study, a finite element (FE) model of composite T-joints is established, which is verified by quasi-static tests to investigate the load bearing capacity and failure modes of composite T-joints under bending loadings with different types of defects, including core material defects, radius floating of the fillet, and debonding defects. It is indicated that the failure modes of T-joints with different kinds of defects under bending loadings are similar, i.e., the delamination occurs firstly at the interface between the filling area and the L-rib before expanding to both sides. Meanwhile, the types of defects exert great effects on the load bearing capacity of T-joints, and the debonding defects in the arc area represent the most dangerous one. Furthermore, the orthogonal test method was adopted to analyze the influence of combined defects on the load bearing capacity of T-joints, and the findings reveal that the most sensitive type of defect is the debonding defects, followed by the radius floating of the fillet, and then core material defects. This result indicates that combined defects have a coupling effect on the load bearing capacity of composite T-joints. This study provides theoretical guidance and technical support for the repair of the defects of composite T-joints.

Failure Mode of Load-bearing Joints in Three-dimensional Braided Composites

Experimental and numerical study of in-plane compressive properties and failure of 3D six-directional braided composites with large braiding angle

Fatigue Behavior of 3D Braided Composites Containing an Open-Hole

Experimental study on the fabrication, high-temperature properties and failure analysis of 3D seven-directional braided composites under compression

Experimental characterization of failure behaviour for three-dimensional woven carbon/carbon composites under pin-loading

Compressive Failure Characteristics of 3D Four-Directional Braided Composites with Prefabricated Holes

X-ray microtomography analysis of the damage mechanisms in 3D circular braided carbon fiber/epoxy resin composite tubes under axial impact compression

Mechanical performance and parameter sensitivity analysis of 3D braided composites joints

Investigation of parameterized braiding parameters and loading directions on compressive behavior and failure mechanism of 3D four-directional braided composites

Experimental study on the mechanical properties of three‐dimensional braided composite circular tubes with preembedded licker‐in

Study on in-plane compression properties and numerical modeling of three dimensional five-directional braided composites

Numerical investigation of tensile behavior of three-dimensional six-directional braided composites

Multiaxial failure mechanism of 3D triple-twill warp-lining woven composites

Tensile Failure Analysis of Carbon Fiber Composite Material L-shaped Joint

A novel mechanical behavior and failure mechanism analysis of 3D six-directional braided composites in liquid nitrogen subjected to compression

Damage and failure analyses of 3D4d braided composite shafts under torsional load and the effects of braid processing parameters on their torsional properties

Investigations on the Mechanical Properties of Composite T-Joints with Defects under Bending Loading

Parameterized meso-scale modeling and experimental study on the tensile damage evolution and strength of 3D five-directional braided composites

Analysis of in-plane compression failure mechanism in carbon fiber braided composite with different off-axial angles

Process-structure-performance modelling and progressive damage analysis of 3D rotary four-directional rectangular braided composites under tensile load

Investigating the Effects of Contact Area and Chamfering on the Failure Behavior of Plain Woven Composite-Metal T-joints