Abstract:The group-Ⅲ nitrides and their related ternary alloys have been becoming the most attractive material for light emitting diodes (LEDs) and laser diodes (LDs) in the UV and blue spectral range. However, the origins of the yellow luminescence (YL), which is commonly observed in almost undoped and n-type GaN, remain unclear. The nature and the role of initial nitridation of sapphire surface and the generation of threading dislocation (TD) are ambiguous too. It is a possible way to resolve the above problems by studying the microstructures and optical properties combining the growth conditions. In this work, two kinds of GaN films were grown by MOCVD under different initial nitridation time (180 seconds for Sample A, and 90s for Sample B). The growth temperature is about 950℃. The cross-sectional transmission electron microscope (TEM) is performed near the GaN/sapphire interface. Corresponding the growth processes, there are three zones in the GaN layer: buffer layer, zone and sound zone. There are haystack-like domains in the faulted zone, in which there are high density of extended defects. The thickness of the faulted zone is about 0.4μm. Just above this region, the defects density is reduced sharply, and the quality of the layer is improved, which is identified by electron diffraction (ED) patterns. In comparison, Sample A shows about an order lower density of extended defects than Sample B, their columnar diameter is larger and its ED pattern is sharper, too. The buffer layer of Sample B is more smooth than Sample A. The appropriate rougher morphology of the buffer layer may cause that the structural disorder between the high-temperature (HT) grown island and the buffer layer is accommodated by Frank and Shockley partial dislocations. However, the TD is likely to propagate into the HT GaN from the smooth surface of the buffer layer grown after extensively nitridation of substrate. According to the position and width of X-ray diffraction peaks of (0002) and (0004), the size of crystalline grain, D and the residual strain could be calculated. The values of(D,e in)of Sample A and B are (175nm,0.167%) and (90nm,0.141%), respectively. Small size of crystalline grain may be advantageous to relieve the lattice and thermal mismatch stress, but it lead to higher density of extended defects. The width of GaN (0002) reflections of Sample A is 4min lower than that of Sample B. This result may be due to the lower screw TD. The higher density of screw TD may widen the GaN (0002) peak in X-ray rocking curve. In room temperature PL spectra, the ratio of band-edge emission intensity to YL one of Sample A is 3 orders larger than that of Sample B. Furthermore the YL in Sample B is stronger and has fine structure, while that in Sample A is nearly invisible in the PL spectrum. The GaN epilayer with high quality exhibits almost no YL emission. It is well known that the YL corresponds to the deformed crystal structure. We assigned that the screw TD and mixed TD are attributed to the YL referring to our XRD results.

Microstructure and optical properties of nanocrystalline GaN embedded in silica matrix

Structure and Photoluminescence of Ge Nanoparticles Embedded in SiO2 Gel Glasses Fabricated at Different Temperatures

Sol–gel preparation of Ge nanocrystals embedded in SiO2 glasses

Photoluminescence of Ge Nanoparticles Embedded in Sio2 Glasses Fabricated by A Sol-Gel Method

Optical Properties of Nanometre AgI–silica Composite Synthesized by a Simple Quenching Method

Nonthermal plasma synthesized freestanding silicon–germanium alloy nanocrystals

From powder to nanowire: A simple and environmentally friendly strategy for optical and electrical GaN nanowire films

Preparation, Doping Modulation and Field Emission Properties of Square-Shaped GaN Nanowires

Optical, Structural, and Synchrotron X-ray Absorption Studies for GaN Thin Films Grown on Si by Molecular Beam Epitaxy

Temperature-Dependent Photoluminescence from GaN/Si Nanoporous Pillar Array

Microstructural and Optical Properties of GaN Films on Nitrided Sapphire Substrates

Formation of Cubic GaN Nanocrystals: A Study of the Thermal Stability of GaP Nanocrystals under Nitrogen

Large-scale Synthesis of Single-Phase, High-Quality GaN Nanocrystallites

Large-scale Fabrication and Luminescence Properties of GaN Nanostructures by a Soft UV-curing Nanoimprint Lithography.

Fabrication and Photoluminescence of Ordered GaN Nanowire Arrays

Structure and Luminescence of A-Plane GaN on R-Plane Sapphire Substrate Modified by Si Implantation*

X-ray Diffraction, Photoluminescence and Secondary Ion Mass Spectroscopy Study of GaN Films Grown on Si(111) Substrate by Vacuum Reactive Evaporation

Defect-pit-assisted Growth of GaN Nanostructures: Nanowires, Nanorods and Nanobelts

Preparation and Properties of Gan Micro-Ribbons on Ga-Diffused Si (111) Substrates

Excitonic Photoluminescence properties of nanocrystalline GaSb and Ga0.62In0.38Sb embedded in silica films

GaN films synthesized through reactively reconstructing Ga_2O_3 films sputtered on Ga-diffused Si substrates