Abstract:The goal of the presented investigation was to assess the impact of surface laser modification with the implementation of nickel and chromium on the microstructure and tribological behaviour of grey iron. Surface laser modification consisted of remelting the surface layer with simultaneous implementation of selected elements. In the first variant of treatment only nickel was implemented and in the second one, a combination of nickel with chromium together. This treatment was performed on an agriculture machine part made of grey iron and working in intensive friction conditions. The constituted surface layer was characterized by about 0.45 mm of depth and a 160 mm2 area of the most exposed to wear of the treated part. In the case of both types of variants, the achieved surface layer microstructure was identified as homogenized with small grains. It involved nickel in the first variant of modification and nickel and chromium in the second one. The attained microstructure with nickel addition was characterized by nearly 800 HV0.1 of hardness (a 3.6-fold increase in comparison to its core material). The approximate hardness of 900 HV0.1 was achieved in the case of the microstructure enriched with nickel and chromium (over a 4-fold increase in comparison to the core material). The roughness of the surface after laser modification was reduced (nearly 3-fold) in comparison to the original surface of the part that was characterized by quite substantial coarseness. The wear test showed that Ni and Cr laser coatings increased resistance to abrasive wear resulting from the modification of the microstructure by the formation of martensite and grain fragmentation. Laser modified parts had a 2.5-fold smaller mass loss than untreated parts. Both types of performed variants: with the implementation of nickel and a combination of nickel and chromium gave comparable effects.

Effect of plasma-arc scanning on the wear resistance of gray iron

Micro-plasma arc surface treatment of gray iron

A Study on the Wear Resistance of Laser Cladding Layers on Grey Iron

Enhancement of Mechanical Properties and Corrosion Resistance of Cast Iron Alloy Using CO2 Laser Surface Treatment

Improving the Properties of Gray Cast Iron by Laser Surface Modification

Study on the effects of laser quenching power and scanning speed on the property of cast iron

Effect of Surface Melting and Chromium Surface Alloying on Wear Behavior of Ductile Iron

Microstructure and Soil Wear Resistance of a Grey Cast Iron Alloy Reinforced with Ni and Cr Laser Coatings

Study on the Effects of GO on the Microstructure and Wear Resistance of CuCrZr Plasma Cladding Coatings

Effects of Nitriding-Quenching and Carburizing-Quenching on Wear Properties of Industrial Pure Iron

Effect of cooling conditions on microstructure evolution and wear behavior of high chromium cast iron hardfacing layer

Investigation on Microstructures and Tribological Characteristic of Laser Remelting Layers

Study on friction and wear behavior of gray cast iron with different carbon content at different temperatures

Surface Physical and Chemical Modification of Pure Iron by Using Atmospheric Pressure Plasma Treatment

Microstructure and wear behavior of arc-shaped 40CrNiMo steel after laser hardening

Friction and wear characteristics of plasma-sprayed WC coatings in dliding against GCr15 steel

Influence of Heat Treatment on Erosive Wear Resistance of High Cr Cast Irons

Repair feasibility and performance enhancement analysis of Fe-based alloy coating on ductile iron surface by high-speed laser cladding

Numerical Optimization and Performance Study of Ni-Based Coatings on Gray Cast Iron Surface by High-Speed Laser Cladding Based on Orthogonal Test

Study of the effect of overlap rate on the failure form, microstructure and wear resistance of multilayer laser cladding on grey cast iron surfaces

Crack resistance and wear resistance of laser clad layer on the surface of cast iron