Abstract:Homogeneous mesoporous lignocellulose aerogels were prepared from hardwood using 1-allyl-3-methylimidazolium chloride (AMImCl) as an ionic liquid (IL) via cyclic liquid nitrogen freezing-thawing (NFT, from -196 degrees C to 20 degrees C) treatment processes. The obtained hydrogels after NFT treatment were solvent-exchanged by acetone, washed with liquid carbon dioxide and then dried by releasing the carbon dioxide at the critical temperature. It was observed that the obtained aerogels after five-cycles of NFT treatment had open-structured 3-dimensional (3D) fibril-like networks. The surface areas and pore size distributions could be adjusted by controlling the NFT treatment cycles. However, the samples treated by common freezing-thawing (FT, from -20 degrees C to 20 degrees C) displayed a film-like 2D structure and low surface area. This may be ascribed to the difference of the assembled 'secondary units' formed during the freezing process. For instance, in the NFT process, 3D-like 'secondary assembly units' were squeezed out by small IL crystals formed during the ultra low temperature freezing process. These 'secondary assembly units' were able to build a large 3D network through the connection and overlap effect with cyclic NFT processes. However, the assembled 2D-like 'secondary assembly units' were squeezed out by large IL crystals in the common FT process due to the slow freezing process and finally were developed to a film-like structure. These 'secondary assembly units' could be linked together in a slow thawing process to form compact aerogels. This study provides a new means to fabricate novel mesoporous lignocellulose aerogels, which is crucial to fully utilize abundant lignocellulose biomass. The homogeneous mesoporous aerogels can be used as highly insulating materials with low thermal conductivity and also have appealing performance in sound absorption and noise reduction properties.

Microstructure of Wood Cell Wall and Preparation Principle of Aerogel-type Wood

Self‐Densification of Highly Mesoporous Wood Structure into a Strong and Transparent Film

Structural Characterization of Lignins from Willow Bark and Wood.

Nanostructurally Controllable Strong Wood Aerogel toward Efficient Thermal Insulation

Directional-Freezing-Assisted In Situ Sol–Gel Strategy to Synthesize High-Strength, Fire-Resistant, and Hydrophobic Wood-Based Composite Aerogels for Thermal Insulation

Top-Down Approach Making Anisotropic Cellulose Aerogels As Universal Substrates for Multifunctionalization

Chemical Structure and Mechanical Properties of Wood Cell Walls Treated with Acid and Alkali Solution

Aerogel nanoarchitectonics based on cellulose nanocrystals and nanofibers from eucalyptus pulp: preparation and comparative study

Lightweight, strong, moldable wood via cell wall engineering as a sustainable structural material

Robust, Fire-Retardant, and Water-Resistant Wood/Polyimide Composite Aerogels with a Hierarchical Pore Structure for Thermal Insulation

Lignocellulose Aerogel from Wood-Ionic Liquid Solution (1-Allyl-3-methylimidazolium Chloride) under Freezing and Thawing Conditions.

Preparation and Comparative Study of Aerogels Based on Cellulose Nanocrystals and Nanofibers from Eucalyptus Pulp

Preparation of mechanically strong and lightweight cellulose aerogels from cellulose-NaOH/PEG solution

Research in porous structure of cellulose aerogel made from cellulose nanofibrils

Fabrication of Mesoporous Lignocellulose Aerogels from Wood Via Cyclic Liquid Nitrogen Freezing–thawing in Ionic Liquid Solution

Strong and Durable Wood Designed by Cell Wall Bulking Combined with Cell Lumen Filling

Wood‐Derived Ultrathin Carbon Nanofiber Aerogels

Facile Preparation of Cellulose Aerogels with Controllable Pore Structure

Cellulose Aerogels Prepared from Cellulose/amimcl Solutions

Metallic Wood through Deep-Cell-Wall Metallization: Synthesis and Applications

Epoxy-Acrylic Polymer In-Situ Filling Cell Lumen and Bonding Cell Wall for Wood Reinforcement and Stabilization