Abstract:Highly porous nano?cellulose aerogels were prepared through a spontaneous physical gelation route by using calcium chloride solution in combination with tert?butyl alcohol solvent displacement and freeze drying technology. According to colloidal stability theory, the existence of calcium chloride could change the original charge distribution of the sol system to improve the gel formation process of the nano particles. Replacing water with tert?butyl alcohol could reduce capillary force, thus reducing the damage to the gel network structure during the drying process as well as lowering the shrinkage rate of aerogel to maintain its three dimensional network structure. The microstructure, spe?cific surface area, pore size distribution, and thermal degradation of resulting aerogel were characterized with scanning electron microscope, micrometrics analyzer and thermo gravietric analyzer, respectively. The prepared nano?cellulose aerogels were white solid and the shrinkage of nano?cellulose aerogels were neglectable. Nano?cellulose aerogel of 3?5% mass ratio exhibited the highest specific surface area up to 174?3 m2/g, and an average pore size of 18?4 nm and weak shrinkage of 7?86%. The isotherm adsorption?desorption curves of nano?cellulose aerogels were of Type II ( IUPAC classification) . The distribution of pore size indicated the meso and macro pores, which was consistent with the results from nitrogen physisorption isotherms. The pore volume, specific surface and the porosity of nano?cellulose aerogels increased while the shrinkage decreased with the increasing cellulose mass ratio. Nano?cellulose aerogel showed a similar thermal degradation behavior as MCC(microcrystalline cellulose) and NCC(nanocrystalline cellu?lose) , while the onset degradation temperature of aerogel was lower than those of MCC and NCC.

Preparation of mechanically strong and lightweight cellulose aerogels from cellulose-NaOH/PEG solution

Ultralight, Elastic, Magnetic and Superhydrophobic Cellulose Nanofibril Based Aerogel with Layer-Support Structure Designed for Both Excellent Oil-Water Separation and Efficient PM2.5 Removal

Facile Preparation of Cellulose Aerogels with Controllable Pore Structure

Research in porous structure of cellulose aerogel made from cellulose nanofibrils

Cellulose aerogels from cellulose–NaOH/PEG solution and comparison with different cellulose contents

Cellulose Aerogels from Aqueous Alkali Hydroxide–Urea Solution

Cellulose Aerogels Prepared from Cellulose/amimcl Solutions

Robust Silica-Cellulose Composite Aerogels with a Nanoscale Interpenetrating Network Structure Prepared Using a Streamlined Process.

Mechanically Strong and Thermally Responsive Cellulose Nanofibers/Poly(N-isopropylacrylamide) Composite Aerogels

Porous Cellulose Aerogels with High Mechanical Performance and Their Absorption Behaviors

Comparative Study of Aerogels Obtained from Differently Prepared Nanocellulose Fibers.

An Efficient and Economic Approach for Producing Nanocellulose-Based Aerogel from Kapok Fiber

Aerogel nanoarchitectonics based on cellulose nanocrystals and nanofibers from eucalyptus pulp: preparation and comparative study

Preparation, characterization and oil adsorption properties of cellulose aerogels from four kinds of plant materials via a NAOH/PEG aqueous solution

Fabrication of nano-cellulose aerogels by freeze drying using tert-butyl alcohol as displacement solvent

Fabrication of Cellulose Aerogel from Wheat Straw with Strong Absorptive Capacity

Enhanced Mechanical Stability and Hydrophobicity of Cellulose Aerogels via Quantitative Doping of Nano-Lignin

Flexible and Transparent Cellulose Aerogels with Uniform Nanoporous Structure by a Controlled Regeneration Process

Facilitated Fabrication of High Strength Silica Aerogels Using Cellulose Nanofibrils As Scaffold.

Transparent Aerogels with High Mechanical Strength Composed of Cellulose-silica Cross-linked networks

Strong, Lightweight, and Shape-Memory Bamboo-Derived All-Cellulose Aerogels for Versatile Scaffolds of Sustainable Multifunctional Materials