Preparation and Properties of C/C-SiC Brake Composites Fabricated by Warm Compacted-in Situ Reaction

Zhuan Li,Peng Xiao,Xiang Xiong

DOI: https://doi.org/10.1007/s12613-010-0348-y

2010-01-01

International Journal of Minerals Metallurgy and Materials

Abstract:Carbon fibre reinforced carbon and silicon carbide dual matrix composites (C/C-SiC) were fabricated by the warm compacted- in situ reaction. The microstructure, mechanical properties, tribological properties, and wear mechanism of C/C-SiC composites at different brake speeds were investigated. The results indicate that the composites are composed of 58wt% C, 37wt% SiC, and 5wt% Si. The density and open porosity are 2.0 g·cm −3 and 10%, respectively. The C/C-SiC brake composites exhibit good mechanical properties. The flexural strength can reach up to 160 MPa, and the impact strength can reach 2.5 kJ·m −2 . The C/C-SiC brake composites show excellent tribological performances. The friction coefficient is between 0.57 and 0.67 at the brake speeds from 8 to 24 m·s −1 . The brake is stable, and the wear rate is less than 2.02×10 −6 cm 3 ·J −1 . These results show that the C/C-SiC brake composites are the promising candidates for advanced brake and clutch systems.