Abstract:AbstractThe search for suitable friction materials for high-speed train is an attractive but difficult problem. In recent years, a variety of different novel friction materials were fabricated to meet the aims of high loads and speeds under ambient environment. Carbon fiber-reinforced carbon composites (C/C), carbon fiber-reinforced silicon carbide composites (C/C-SiC) and metallic composites fabricated by powder metallurgy are three excellent materials among them. Here a comparison of these three different materials working as brake pads, coupled with high-density C/C-SiC brake disk, was described. All the experiments were conducted using the same procedure with increasing initial braking speed (the rotation speed of brake disk at the beginning of braking process) from 30 to 59 m/s and constant load of 1.25 MPa, simulating the real working condition of high-speed train. The coefficient of friction (COF) and wear rates of three materials were compared and analyzed. During experiments, the COF of metallic and C/C pads remains nearly constant at 0.31 and 0.22, respectively, with increasing braking speed, while that of C/C-SiC exhibits a parabola. These different trends of COF may be attributed to the distinctive forming processes of friction film on the top of contact surfaces. Meanwhile, the wear rates of metallic composites increase rapidly from 683 to 1803 mm3/MJ with initial braking speed, while C/C-SiC presents the highest wear loss of 1887 mm3/MJ at 49 m/s and lowest value of 315 mm3/MJ at 59 m/s. Interestingly, the wear rate of C/C composites, due to the appropriate bonding strength of matrix/fiber and relatively high shear stress, decreases from 3698 to 903 mm3/MJ with increasing initial braking speed, which does not consist with pre-existing paper. Thus, metallic pads presented the lowest wear rates at lower speed (<49 m/s) but the highest at high speed, while C/C-SiC composite pads showed the greatest wear resistance at high speed. This investigation of three different friction materials will enhance our understanding of these friction materials and benefit the selection and safe application of high-speed train friction materials.

Friction and Wear Behaviors of C/C-SiC Composites Containing Ti3SiC2

Mechanical and tribological properties of C/C–SiC ceramic composites with different preforms

Water-Lubricated Friction Properties of C/C-SiC Composites with Different SiC-Phase Contents Fabricated by RMI

Effect of TiC Coated MWCNT Content on Friction and Wear Behavior of MWCNT–Ti3SiC2 Composites

The Microstructure and Wear Characteristics of Cu–Fe Matrix Friction Material with Addition of SiC

Synthesis and Tribological Behaviors of Ti 3 SiC 2 Material Prepared by Vacuum Sintering Technique

Effect of graphitization on microstructure and tribological properties of C/SiC composites prepared by reactive melt infiltration

Preparation of C/C-SiC Brake Materials with Low Cost and High Friction Performance

Friction and Wear Properties of Carbon/carbon Composites with Different Martix Carbon

Investigation of Impact of C/Si Ratio on the Friction and Wear Behavior of Si/SiC Coatings Prepared on C/C-SiC Composites by Slurry Reaction Sintering and Chemical Vapor Infiltration

Friction And Wear Properties Of Aluminum Matrix Composites And Its Application

DRY SLIDING TRIBOLOGICAL CHARACTERISTICS OF SiC PARTICLE-REINFORCEDALUMINUM COMPOSITES AGAINST SEMI-METALLIC FRICTIONAL MATERIAL

Microstructures and properties of C/C–SiC composites derived from different gaseous carbon matrix precursors

Tribological Properties of Ti3SiC2 Coupled with Different Counterfaces

Fading behavior and wear mechanisms of C/C–SiC brake disc during cyclic braking

Tribo-oxide Competition and Oxide Layer Formation of Ti3SiC2/CaF2 Self-Lubricating Composites during the Friction Process in a Wide Temperature Range

Ceramic waste SiC particle-reinforced Al matrix composite brake materials with a high friction coefficient

Sintering and Tribological Properties of Ti3SiC2-TiSix Composite Sintered by High-Pressure High-Temperature Technology

Tribological behaviour of C/C–SiC composites—A review

Microstructure and Wear Behavior of Ti-xFe-SiC In Situ Composite Ceramic Coatings on TC4 Substrate from Laser Cladding

Comparison of Friction and Wear Behavior Between C/C, C/C-SiC and Metallic Composite Materials