Abstract:This paper studied the role of bimodal-grained structure in strengths and asymmetry behaviors of Mg-15Gd-1Zn-0.4Zr (wt%) alloys under the as-extruded, compressive-yielded and fractured conditions. The bimodal-grained structure consisting of fine recrystallized grains and coarse un-recrystallized grains formed when the alloys were extruded with relatively low temperature. Compared with the equiaxed structure, the bimodal-grained structure possessed higher tensile strength attributed to the fine recrystallized grains plus the strong and hard un-recrystallized texture with its basal planes nearly parallel to the loading direction. However, the bimodal-grained structure weakened the ultimate compressive strength, because the un-recrystallized texture is favorable for tensile twining in the compressive test. Eventually, the aged sample with the bimodal-grained structure exhibited ultra-high tensile yield strength and ultimate tensile strength of 465 MPa and 524 MPa, respectively. Especially, the inhomogeneous bimodal-grained structure with stronger texture resulted in extraordinary low compressive-tensile yield asymmetries of 0.99 and 0.98 compared with those (from 1.09 to 1.48) of the homogeneous equiaxed structures with relatively random textures, because the fine recrystallized grains in the bimodal-grained structure undertook major deformation by slips and suppressed twining before the yield points in the mechanical tests. The relationship between the microstructures and properties allows us to produce high tensile strength Mg components by applying low extrusion temperature and obtaining bimodal-grained structure.

Processing and Properties of Mg–6Gd–1Zn–0.6Zr

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

Microstructure and Mechanical Properties of Mg-2.6Sm-1.3Gd-0.6Zn-0.5Zr Alloy

Microstructures and Mechanical Properties of Mg–10Gd–6Y–2Zn–0.6Zr(wt.%) Alloy

Microstructures and Tensile Properties of Mg-6Gd-3Y-1.4Zn-0.4Zr Alloys

Microstructure and strengthening mechanisms of a cast Mg–1.48Gd–1.13Y–0.16Zr (at.%) alloy

Achieving Enhanced Mechanical Properties in Mg-Gd-Y-Zn-Mn Alloy by Altering Dynamic Recrystallization Behavior Via Pre-Ageing Treatment

Formation of an abnormal texture in Mg-Gd-Y-Zn-Mn alloy and its effect on mechanical properties by altering extrusion parameters

Effect of Zn Addition on Microstructure and Mechanical Properties after Extrusion, Rolling and Ageing in Mg-9Gd-3Y-0.5Zr Alloys

Effect of Zn Addition on Microstructure and Mechanical Properties of Mg–9Gd–3Y–0.5Zr Alloy

Effect of Solid Solution and Aging Treatments on the Microstructures Evolution and Mechanical Properties of Mg–14Gd–3Y–1.8Zn–0.5Zr Alloy

The microstructure evolution and abnormal yield asymmetry of extruded Mg-10Gd-0.5Zr alloy

Ex-situ EBSD Analysis of Yield Asymmetry, Texture and Twinning Development in Mg–5Li–3Al–2Zn Alloy During Tensile and Compressive Deformation

Microstructure and mechanical properties of Mg-12Gd-5Y-1Sm-0.5Zr alloy

The Role of Bimodal-Grained Structure in Strengthening Tensile Strength and Decreasing Yield Asymmetry of Mg-Gd-Zn-Zr Alloys

Microstructure and Mechanical Properties of Mg–Gd–Y–Zn–Zr Alloy Sheets Processed by Combined Processes of Extrusion, Hot Rolling and Ageing

Effects of extrusion ratio and subsequent heat treatment on the tension-compression yield asymmetry of Mg-4.58Zn-2.6Gd-0.18Zr alloys

Microstructures and Mechanical Properties of a Mg–9Gd−3Y−0.6Zn−0.4Zr (wt.%) Alloy Modified by Y-rich Misch Metal

Microstructures and Mechanical Properties of Mg-10Gd-3Y-2Zn-0.5Zr Alloy

Effects of Zn on the Microstructures and Mechanical Properties of Mg–3Sm–0.5Gd–xZn–0.5Zr (x = 0, 0.3 and 0.6) Alloy