Abstract:The transformation-assisted consolidation under pressure has been demonstrated to be a promising method to fabricate the nano or submicron polycrystalline ceramic materials. The high pressure suppresses the long-range diffusion of the atoms and, consequently, restrains the grain coarsening. The new phases produced at high pressure could show finer grains under the appropriate thermodynamic conditions, which are not subject to the grain size of the raw materials. Ceramic materials exhibit the existence of the transformations under certain thermodynamic conditions and the formation of new phases generally undergoes the nucleation and growth. In the present work, monoclinic microcrystal ZrO2 with average grain size of 2 µm and Y2O3 with average grain size of 50 nm were mixed in molar ratio of 97∶3. The preparation of the samples was carried out by sintering at 5.5 GPa and temperatures of 800–1700 °C using the high pressure cubic cell, and the sample characterization was performed via the X-ray diffraction, scanning electron microscope and transmission electron microscopy. It was found that the monoclinic and submicron tetragonal composite polycrystalline ZrO2 in bulk is obtained under high pressure and high temperature. The average grain size of tetragonal ZrO2 fabricated at 1200, 1400, 1600 and 1700 °C is (145±62) nm, (246±165) nm, (183±62) nm and (245±107) nm, respectively. The synthesis of the fine-grained polycrystalline materials by the transformation under high pressure can solve the problems of agglomeration, adsorption and grain coarsening caused by the nanopowders as the starting materials in the conventional approach, which would be an alternative route to fabricate the fine-grained polycrystalline materials with the enhanced performances.

Transformation and Fracture of Zro2-Based Ceramics at Low-Temperatures

Strength And Toughness Of Zro2-Based Ceramics At Cryogenic Temperatures

[Study on Low Temperature Degradation of Dental Zirconia Ceramic].

Effect of Y2O3 Contents and Grain Sizes on the Mechanical Properties and Transformation of Zirconia Ceramics at Cryogenic Temperatures

Phase Transformation and Exceptional Mechanical Properties of 3Y-TZP at Cryogenic Temperature

Fracture Toughness of 3 Mol% Yttria-Stabilized Zirconia at Cryogenic Temperatures

Fabrication of Submicron Tetragonal Polycrystalline ZrO2 by the Transformation of Micro Monoclinic ZrO2 under High Pressure

R‐Curve Behavior of 3Y‐TZP at Cryogenic Temperatures

Toughening Mechanisms of ZTA Ceramics at Cryogenic Temperature (77 K)

Fracture Strength and Dynamic Elastic Modulus of Ce‐ and Er‐TZP at Low Temperature

Influence of Low Temperature Aging on the Flexural Strength of Y-TZP Ceramics

Brittle-to-Ductile Transition and High-Temperature Deformation in ZrO<SUB>2</SUB>(Y<SUB>2</SUB>O<SUB>3</SUB>) and Al<SUB>2</SUB>O<SUB>3</SUB> Ceramics as Evaluated by Small Punch Test

Diffusionless Cubic-To-Tetragonal Phase-Transition And Microstructural Evolution In Sintered Zirconia Yttria Ceramics

Mechanical and Wear Properties of Low-Temperature-Sintered 3Y-TZP Ceramics

Brittle-to-ductile transition and high-temperature deformation in ZrO2(Y2O3) and Al2O3 ceramics as evaluated by small punch test

Microstructure and Mechanical Properties of ZrO2-2 Mol% Y2O3 Ceramics

Phase Transformation and Slow Crack Growth Study of Y-TZP Dental Ceramic

Slow Crack Growth Behavior of 3Y-TZP in Cryogenic Environment Using Dynamic Fatigue and Indentation Technique

Microstructural dependence of aging induced phase transformation in Y2O3 partially stabilized ZrO2 polycrystals

Critical grain size and fracture toughness of 2 mol.% yttria-stabilized zirconia at ambient and cryogenic temperatures

The Effect of Sintering Temperature on Phase-Related Peculiarities of the Microstructure, Flexural Strength, and Fracture Toughness of Fine-Grained ZrO2–Y2O3–Al2O3–CoO–CeO2–Fe2O3 Ceramics