Abstract:NiAl intermetallics is considered to be a potential high temperature structural material based on a high melting point, low density, high thermal conductivity, excellent oxidation and hot-corrosion resistance at elevated temperatures [1–4], but its high temperature strength is insufficient for the majority of actual applications. The tensile ductility and fracture toughness at ambient temperatures are often also unsatisfactory [5, 6]. The solid solution strengthening, precipitation strengthening, directional solidification and single crystal technique have been explored to improve its high temperature strength. Although significant progress has been achieved, the ambient tensile ductility and fracture toughness often deteriorate as a result. On the other hand, the ductility and toughness can also be improved by microalloying, macroalloying and plastic secondary phase additions, but this is at the expense of the strength [4–7]. In other words, it is very difficult to compromise its high temperature strength and ambient temperature ductility. This severely restricts its operating temperature and deteriorates its machinability. It is significant to explore novel fabricaturing techniques for NiAl intermetallic alloy to improve its comprehensive mechanical properties. Preparing intermetallic matrix composite is an effective method to produce engineering NiAl intermetallic alloy and to improve its high temperature strength and retain ambient temperature ductility simultaneously [8, 9]. Good ductility can be obtained through adequately alloying the intermetallic matrix while the strength is improved with the reinforcements. The casting, combustion synthesis, powder metallurgy and mechanical alloying are major methods for preparing NiAl intermetallic matrix composites. Nevertheless, in many cases, the mechanical bonding due to no interfacial reaction, or the brittle reactive products existing at the interface between matrix and reinforcement due to excessive interfacial reaction often result in weak interfacial bonding so that whole properties

Nickel Aluminide (ni3al) Fabricated by Reactive Infiltration

Fabrication and mechanical properties of the NiAl sheet with a 3-dimensional network structure prepared by Ni nets and Al foils

In situ fabrication of α-Al2O3 and Ni2Al3 reinforced aluminum matrix composites in an Al–Ni2O3 system

Formation of Al<sub>3</sub>Ni nanofibers in an Al-based metal matrix composite fabricated by reaction sintering

Microstructure and Mechanical Properties of Ni3Al Fabricated by Thermal Explosion and Hot Extrusion

Investigating the Influence of Al Contents on Microstructure and Mechanical Properties of Ni 3 Al Superalloy Fabricated by Twin Wire‐Based Direct Arc Energy Deposition

In Situ Fabrication and Mechanical Properties of Al–AlN Composite by Hot Extrusion of Partially Nitrided AA6061 Powder

Direct Laser Fabricated in Situ TiC Particulate Reinforced Ni30Al20Fe Intermetallic Matrix Composite

Formation of Al 3 Ni Nanofibers in an Al-Based Metal Matrix Composite Fabricated by Reaction Sintering

Fabrication of Al-Ni nanofibers by selective etching

The synthesis and mechanical property evaluation of Ni/Ni3Al microlaminates

Pressureless Infiltration and Resulting Mechanical Properties of Al-AlN Preforms Fabricated by Selective Laser Sintering and Partial Nitridation

Fabrication and Mechanical Properties of Microalloyed and Ceramic Particulate Reinforced NiAl-based Alloys

Fabrication of NiAl alloy hollow thin-walled component through hot gas forming of Ni/Al laminated tube and conversion process

Synthesis Mechanism and Strengthening Effects of Laminated NiAl by Reaction Annealing

The Oxidation of Nanocrystalline Ni3al Fabricated by Mechanical Alloying and Spark Plasma Sintering

Characterization of Ni3Al Alloy Fabricated by Thermal Explosion and Hot Extrusion Process

Fabrication of as-cast Al matrix composite reinforced by Al2O3/Al3Ni hybrid particles via in-situ reaction and evaluation of its mechanical properties

Microstructural evolution and mechanical properties of Ni/Al reactive nanolaminates with different NixAly intermetallic phases

Fabrication and Characterization of Nickel‐Aluminide Cladding by Dual Wire arc Additive Manufacturing

Microstructure and mechanical properties of a novel polycrystalline Ni3Al-based intermetallic alloy