Formation of Al 3 Ni Nanofibers in an Al-Based Metal Matrix Composite Fabricated by Reaction Sintering

Peng Yu,Cheng-Ji Deng,Nan-Gang Ma,Dickon L. L. Ng

DOI: https://doi.org/10.1557/JMR.2004.0154

IF: 2.7

2004-01-01

Journal of Materials Research

Abstract:We developed an Al 2 O 3 and Al 3 Ni intermetallic reinforced Al-based metal matrix composite by sintering an Al-20 wt% NiO powder compact at 1000 °C. Differential thermal analysis showed that a two-step reaction took place between Al and NiO in the temperature range 600–650 °C. The initial stage was a solid-state reaction, but it was soon paused by the newly formed Al 2 O 3 and Al 3 Ni phases that separated the Al and NiO grains. A liquid–solid reaction was later resumed as the temperature was increased above the eutectic temperature of Al–Al 3 Ni at 640 °C when molten Al–Ni appeared. When the molten sample was quenched to room temperature, a two-phase Al–Al 3 Ni eutectic was found in the sample. In comparison with the air-quenched and the oil-quenched samples, the sizes of proeutectic Al 3 Ni grains and Al–Al 3 Ni eutectic phases in the salt-solution-quenched sample were much finer. The eutectic contained Al 3 Ni nanofibers with a diameter of approximately 50 nm. A reaction model of Al and NiO was proposed. A thermodynamic model was also proposed to describe the formation of the composite.