Preparation of Zinc-Doped Silica Gel Materials and Their Adsorptive Performance

LIU Deng-wei,HE Yong-jun,ZHANG Chao,ZHANG Lu

2011-01-01

Abstract:Zn-doped silica gel adsorbents were prepared by dipping and hydrolysis of water glass and zinc salts with ceramic fibers as substrates.The products were characterized by scanning electron microscopy(SEM),Fourier transform infrared spectroscopy(FT-IR) and specific surface area analyzer.The influence of the preparation conditions,such as soaking time,soaking temperature,zinc salt concentration,the amount of acid and reaction temperature,on the adsorptive performance of the materials were investigated.SEM images revealed that the particles of Zn-doped silica gel were well scattered on the surface and in the apertures of the ceramic fibers.In the FT-IR spectra,the peak at about 829cm-1 was attributed to the Zn—O—Si linkage of the Zn-doped silica gel.The adsorptive performance of Zn-doped silica gel adsorbents was much higher than that of the ordinary silica gel.The optimized reaction condition for the preparation of Zn-doped silica gel was as follows: soaking time was 60min,dipping temperature was 20℃,zinc content was 30%,reaction temperature was 60℃,and the amount of the added hydrochloric acid was 1.5mL.