Synthesis of Styrene-Acrylate Latex with Gradient Structure
Su Hui,Xie Delong,Zhang Xinya,Chen Huanqin
DOI: https://doi.org/10.3969/j.issn.0253-4312.2011.09.012
2011-01-01
Abstract:Styrene-acrylate latex with hard core-soft shell structure was prepared by gradient emulsion polymerization technology,using styrene(St),butyl acrylate(BA) as core monomers,and methyl methacrylate(MMA),butyl acrylate(BA) as shell monomers,methacrylic acid(MAA),hydroxypropyl methacrylate(HPMA) as functional monomers.The effects of emulsion polymerization technology,emulsifiers,initiator,reaction temperature and functional monomers on the properties of latex were studied.The results showed that the most stable polymerization process and optimum comprehensive properties of latex with less gel formation could be reached when the mass ratio of DSB/OP-10 was 2∶1,the mass of emulsifier,initiator,functional monomer were 1%,0.5%,4% of monomers respectively,the reaction temperature was 80 ℃ and that typical core-shell structure emulsion with lower MFT could be prepared by gradual seed emulsion polymerization.Styrene-acrylate copolymers' chemical structure were characterized by IR,and the particle morphology was observed by TEM,which further verified core-shell structure of the particles.