Inversion of Phase Morphology in Polymer-Blend Thin Films on Glass Substrates

Qi Zong,Zhi Li,Xuming Xie

DOI: https://doi.org/10.1002/macp.200300235

IF: 2.996

2004-01-01

Macromolecular Chemistry and Physics

Abstract:The phase-morphology inversion in two blend systems of polystyrene/poly(methyl methacrylate) (PS/PMMA) and polystyrene/poly(epsilon-caprolactone) (PS/PCL) has been studied after their thin films were prepared on glass substrates by spin-coating from a co-solvent tetrahydrofuran (THF). Phase-contrast microscopy (PCM), scanning-electron microscopy (SEM) equipped with energy dispersive X-ray spectroscopy (EDS), and atomic force microscopy (AFM) were used to obtain information on the morphology of the thin films during heat treatment. It was found that the PMMA-rich and PCL-rich phases are always continuous after annealing in either of the PS/PMMA and PS/PCL blend thin films, even though the PMMA and PCL are minor components in the blends. This should result from the better wetting abilities of PMMA and PCL on a glass substrate than PS in the blends. The effect of the viscosity in the evolution of the phase structure was also investigate by changing the molecular weight of PS in the PS/PCL blend thin films. Further more, it is found that the phase-separation process and the wetting phenomenon of the blends on the glass substrate can be strongly suppressed after adding PS-block-PMMA diblock copolymer to the PS/PMMA blend system as a compatibilizer.