Epitaxial Growth and Rectification Characteristics of Double Perovskite Oxide La2nimno6 Films on Nb-Srtio3 Single Crystal Substrates

G. Y. Gao,Y. Wang,Y. Jiang,L. F. Fei,N. Y. Chan,H. L. W. Chan,W. B. Wu

DOI: https://doi.org/10.1016/j.tsf.2011.03.137

IF: 2.1

2011-01-01

Thin Solid Films

Abstract:High-quality thin films of double perovskite La2NiMnO6 (LNMO) were epitaxially grown on Nb-doped SrTiO3 (NSTO) substrates by pulsed laser deposition. The films were found to undergo a ferromagnetic-to-paramagnetic transition at ~280K, which is consistent with the literature report. In the electrical measurements, typical rectifying behavior was observed in the LNMO/NSTO heterojunction. The diffusion voltage (VD) increases linearly with temperature (T) during cooling until T=170K. At T<170K, VD increases at a higher rate and the VD–T relationship becomes non-linear. A disordered phase related spin polarization was used to understand such behaviors in the heterojunctions.