Improvement of NH3 resistance over CuO/TiO2 catalysts for elemental mercury oxidation in a wide temperature range

Jiayin Li,Qingru Wu,Yuanyuan Wang,Huazhen Chang,Lei Ma
DOI: https://doi.org/10.1016/j.cattod.2020.05.029
IF: 5.3
2021-09-01
Catalysis Today
Abstract:<p>In this study, the effects of ammonia (NH<sub>3</sub>) were explored for catalytic oxidation of elemental mercury (Hg°) over CeO<sub>2</sub>/TiO<sub>2</sub>, CuO/TiO<sub>2</sub>, Fe<sub>2</sub>O<sub>3</sub>/TiO<sub>2</sub>, and V<sub>2</sub>O<sub>5</sub>-WO<sub>3</sub>/TiO<sub>2</sub> catalysts. In the presence of 50 ppm NH<sub>3</sub>, the results showed that CuO/TiO<sub>2</sub> catalysts could still maintain 98-100% of Hg° conversion in the range of 100–400 °C, while the catalytic performance of other catalysts was significantly inhibited by NH<sub>3</sub> in the same temperature range. NH<sub>3</sub> resistance was observed on CuO/TiO<sub>2</sub> catalysts. The catalysts were further characterized by means of XRD, H<sub>2</sub>-TPR, XPS, NH<sub>3</sub>-TPD, BET, and in-situ DRIFTS. For the CuO/TiO<sub>2</sub> catalysts, Cu(II) was the primary Cu species that conducive to the reducibility properties. The strong reducibility properties of the catalysts were beneficial for the catalytic reaction. The mechanism of NH<sub>3</sub> resistance in Hg° oxidation over CuO/TiO<sub>2</sub> catalysts was proposed. At low-temperature range (lower than about 250 °C), abundant weak acidic sites contributed to the superior Hg° adsorption capacity. The Hg° oxidation activity was enhanced correspondingly. At high-temperature range (from about 250 to 400 °C), the Hg° oxidation performance was mainly affected by the oxidation of NH<sub>3</sub>. The main product of NH<sub>3</sub> oxidation was NO<sub>2</sub>, which could promote Hg° oxidation activity.</p>
chemistry, physical,engineering, chemical, applied
What problem does this paper attempt to address?