Abstract:High undercooling rapid solidification process has a significant impact on the solidified microstructure and mechanical properties of materials. In this study, particles with a diameter range between 100 and 1100 μm of ternary Zr 50 Cu 40 Al 10 and Zr 49 Cu 46 Al 5 alloys were prepared by a drop tube. The evolution process of particle-solidified microstructure with decreasing particle diameter was analyzed using XRD, SEM, and TEM. For Zr 50 Cu 40 Al 10 alloy, the solidified microstructure in the particle diameter ranges of 200–1100 μm is composed of an amorphous phase and a primary B2-ZrCu high-temperature metastable phase. As the particle diameter reduces, the retained crystalline phase in the solidified microstructure decreases progressively, and the dendrite grain length gradually becomes finer. When the particle diameter is reduced to below 200 μm, the crystalline phase has completely disappeared, and the solidified microstructure evolves into a completely amorphous structure. For Zr 49 Cu 46 Al 5 alloy, in the particle diameter range of 400–1100 μm, the solidified microstructure consists of primary B19'-ZrCu phase, a small amount of Cu 10 Zr 7 phase and Zr 14 Cu 51 phase. As the particle diameter reduces, a grain refinement phenomenon also occurs in the solidified microstructure and the dendritic morphology changes from equiaxed grain to rod-shaped dendrite. The amorphous phase appears when the particle diameter is lowered to 470 μm and solidified microstructure evolves into a completely amorphous structure as the particle diameter is reduced to 146 μm. The nanoindentation results show that the micromechanical properties of amorphous composite microstructures are superior to the single component composition of crystalline or amorphous phase for Zr 50 Cu 40 Al 10 and Zr 49 Cu 46 Al 5 alloys. The reinforcement effect on the amorphous phase is related to the content of the second crystalline phase. Moreover, under similar particle diameters, the mechanical properties of Zr 50 Cu 40 Al 10 particles are always better than those of Zr 49 Cu 46 Al 5 particles.

Nanocrystalline Zr3Al made through amorphization by repeated cold rolling and followed by crystallization

Bulk Nanostructure Formation Directly From The Multicomponent Alloy Melt

Nanocrystallization of Pure Zr Via Room Temperature Rolling Deformation

Crystallization of Amorphous Zr60Al15Ni25 Alloy

Crystallization process of Zr60Ni25Al15 amorphous alloy

Nanocrystal composites in Zr–Nb–Cu–Al metallic glasses

Nano-sized amorphous alumina particles obtained by ball milling ZnO and Al powder mixture

Effect of Rolling Deformation on the Structure of Bulk Zr60cu30al10 Amorphous Alloy

Deformation behavior of Zr-based bulk nanocrystalline amorphous alloys

Decomposition of Amorphous Zr41ti14cu12.5ni10be22.5 Alloy: As Investigated by Small Angle Neutron Scattering

Nanocrystalline structural evolution in Fe90Zr7B3 soft magnetic material

Crystallization Behavior of Zr55al10ni5cu30 Amorphous Alloys with Different Morphologies and Thermal History Conditions

Influence of rolling on the precipitation of icosahedral quasicrystalline phase in Zr-Al-Ni-Cu-Ag amorphous alloy

In Situ Tem Investigation of Amorphization and Recrystallization of Zr(Fe,Cr,Nb)(2) Precipitates under Ne Ion Irradiation

Structure Evolution of Bulk Zr60Cu20Pd10Al10 Amorphous Alloy During Rolling Deformation

AMORPHOUS AND NANOCRYSTALLINE ZrO2·Y2O3(15%) STUDIED BY EXTENDED X-RAY ABSORPTION FINE STRUCTURE

Atomic and electronic structure of amorphous Al–Zr alloy films

Nanocrystalline Composites with High Strength Obtained in Zr–Ti–Ni–Cu–Al Bulk Amorphous Alloys

Crystalline and amorphous microstructure evolution of Zr-Cu-Al ternary alloys solidified in drop tube

Amorphization Of Zr-Al Under Mechanical Alloying At Different Temperatures: A Re-Entrant Melting Phenomenon

Texture Evolution and Temperature-Dependent Deformation Modes in Ambient- and Cryogenic-Rolled Nanolayered Zr-2.5Nb