Abstract:As tellurides and selenides of Bismuth are extensively used thermoelectric materials in the low-temperature range with refrigeration application, A concerted effort is put forth to boost the ZT by co-doping the pristine Bi 2 Se 3 with antimony (Sb) on cation end and tellurium (Te) on anion side of the compound. The double sintered solid-state reaction method is employed in the preparation of Bi 2 Se 3 and (Bi 1− x Sb x ) 2 Se 2.7 Te 0.3 polycrystalline pellets, with x = 0.02, 0.04, and 0.06. The sample exhibits a rhombohedral structure with the space group of R m. FESEM and EDAX analysis are used to confirm surface morphology and elemental composition of the produced samples. The thermoelectric measurements for the pristine and co-doped samples were conducted by the physical property measurement system as well as a considerable increase in the Seebeck coefficient of − 115 μV/K is observed for 0.02 doping of the Sb which is 4.2 times greater than as for pristine (S = − 28 μV/K). Higher concentration doping ( x = 0.04, 0.06) has not reflected any Seebeck coefficient advancement. In contrast, the lowest total thermal conductivity at a low-temperature regime (< 50 K) is observed for x = 0.06 doping concentration which at near room temperature increases beyond the pristine thermal conductivity; whereas, x = 0.02, 0.04 doping concentration shows a decrement in total thermal conductivity at low, at room temperature region the values are almost equivalent to that of pristine. The co-doped samples' electrical resistivity is substantially less than pristine sample. The highest power factor of 3 × 10 –4 μW/mK 2 is obtained for the x = 0.02 sample. The highest ZT value for the x = 0.02 sample is almost 28 times more than a pristine sample. We conducted a study where we combined experimental and DFT methods to investigate thermoelectric properties incorporated into pristine and doped with antimony and tellurium on Bi 2 Se 3 . We have employed this combination to investigate the partial density of states, Seebeck coefficient, power factor using the Boltzmann transport equation. Theoretical thermoelectric data were derived and compared to experimental observations. Hence, using combined experimental and theoretical investigations helps to predict with higher accuracy of thermoelectric properties of semiconducting materials.

Realizing synergistic optimization of thermoelectric properties in n-type BiSbSe3 polycrystals via co-doping zirconium and halogen

Enhancing thermoelectric performance of BiSbSe3 through improving carrier mobility via percolating carrier transports

Synergistic optimization of the thermoelectric performance of BiSbSe3 using doping and multi-scale defect engineering

Promoted thermoelectric performance of (Ag, Na) co-doped polycrystalline BiSe by optimizing the thermal and electrical transports simultaneously

Electrical property enhancement and lattice thermal conductivity reduction of n-type Mg3Sb1.5Bi0.5-based Zintl compound by In&Se co-doping

Synergistically enhanced thermoelectric properties in n-type Bi6Cu2Se4O6 through inducing resonant levels

Significantly enhanced thermoelectric figure of merit of n-type Mg3Sb2-based Zintl phase compounds via co-doped of Mg and Sb site

Synergistic Effects of Cui Doping on Enhancing Thermoelectric Performance for N-Type Bi 2O 2se Fabricated by Mechanical Alloying

A comprehensive experimental and DFT analysis on thermoelectric properties of Sb, Te co-doped Bi2Se3 polycrystals

Modulation Doping Leads to Optimized Thermoelectric Properties in n‐Type Bi6Cu2Se4O6 due to Interface Effects

Rational triple optimizations boost near-room-temperature thermoelectric performance of BiSe

Na/Bi-co-doping and Heterogeneous Interfaces Leading to Enhanced Thermoelectric Performance of P-Type Mg3Sb2-based Zintls

Thermoelectric Performance of P-Type Zone-Melted Se-doped Bi 0.5 Sb 1.5 Te 3 Alloys

Thermoelectric performance improvement of p-type Mg3Sb2-based materials by Zn and Ag co-doping

Synergistic Optimization of Thermoelectric Performance in SnSe2 through co-doping: Anionic Vacancy Formation and Band Engineering

Realizing high doping efficiency and thermoelectric performance in n-type SnSe polycrystals via bandgap engineering and vacancy compensation

Lattice expansion enables interstitial doping to achieve a high average ZT in n‐type PbS

Carrier Concentration Optimization for Thermoelectric Performance Enhancement in N-Type Bi2O2Se

Synergistically enhanced thermoelectric properties of Bi2S3 bulk materials via Cu interstitial doping and BiCl3 alloying

Synergistical Enhancement of Thermoelectric Properties in N‐type Bi2O2Se by Carrier Engineering and Hierarchical Microstructure

Synergistically optimizing carrier and phonon transport properties in n-type PbTe through I doping and SnSe alloying