Abstract:Medical bone implant magnesium (Mg) alloys are subjected to both corrosive environments and complex loads in the human body. The increasing number of hyperglycemic and diabetic patients in recent years has brought new challenges to the fatigue performance of Mg alloys. Therefore, it is significant to study the corrosion fatigue (CF) behavior of medical Mg alloys in glucose-containing simulated body fluids for their clinical applications. Herein, the corrosion and fatigue properties of extruded Mg-Zn-Zr-Nd alloy in Hank's balanced salt solution (HBSS) containing different concentrations (1 g/L and 3 g/L) of glucose were investigated. The average grain size of the alloy is about 5 μm, which provides excellent overall mechanical properties. The conditional fatigue strength of the alloy was 127 MPa in air and 88 MPa and 70 MPa in HBSS containing 1 g/L glucose and 3 g/L glucose, respectively. Fatigue crack initiation points for alloys in air are oxide inclusions and in solution are corrosion pits. The corrosion rate of the alloy is high at the beginning, and decreases as the surface corrosion product layer thickens with the increase of immersion time. The corrosion products of the alloy are mainly Mg(OH) 2 , MgO and a small amount of Ca-P compounds. The electrochemical results indicated that the corrosion rate of the alloys gradually decreased with increasing immersion time, but the corrosion tendency of the alloy was greater in HBSS containing 3 g/L glucose. On the one hand, glucose accelerates the corrosion process by adsorbing large amounts of aggressive Cl − ions. On the other hand, glucose will be oxidized to form gluconic acid, and then reacts with Mg(OH) 2 and MgO to form Mg gluconate, which destroys the corrosion product film and leads to the aggravation of corrosion and the accumulation of fatigue damage.

Influence of Glucose on Corrosion Fatigue and Cytocompatibility of Mg–Zn–Zr–Y Alloy

Fatigue and Corrosion Fatigue Properties of Mg–Zn–Zr–Nd Alloys in Glucose-Containing Simulated Body Fluids

In Vitro Corrosion of Mg–Ca Alloy — the Influence of Glucose Content

Microbial ingress and in vitro degradation enhanced by glucose on bioabsorbable Mg–Li–Ca alloy

In Vitro Corrosion and Biocompatibility of Binary Magnesium Alloys.

Effects of Inorganic Ions, Organic Particles, Blood Cells, and Cyclic Loading on in Vitro Corrosion of Mg Al Alloys

Influence of load frequency and corrosive environments on fatigue behavior of as-extruded Mg–Zn–Zr–Nd alloy

Corrosion Fatigue Behaviors of Two Biomedical Mg Alloys-Az91d and We43-In Simulated Body Fluid

In Vitro Degradation of Pure Mg in Response to Glucose.

In Vitro Degradation, Hemolysis And Mc3t3-E1 Cell Adhesion Of Biodegradable Mg-Zn Alloy

Mechanical properties, corrosion, and biocompatibility of Mg-Zr-Sr-Dy alloys for biodegradable implant applications

In Vitro Degradation Performance and Biological Response of a Mg–Zn–Zr Alloy

Mechanical properties and corrosion behavior of Mg-Gd-Ca-Zr alloys for medical applications

The Influence of Zn Content on the Corrosion and Wear Performance of Mg-Zn-Ca Alloy in Simulated Body Fluid

Corrosion Resistance and Cytocompatibility of Biodegradable Surgical Magnesium Alloy Coated with Hydrogenated Amorphous Silicon.

On the Corrosion Fatigue of Magnesium Alloys Aimed at Biomedical Applications: New Insights from the Influence of Testing Frequency and Surface Modification of the Alloy ZK60

Stress corrosion cracking and corrosion fatigue characterisation of MgZn1Ca0.3 (ZX10) in a simulated physiological environment

Microstructure, Mechanical Properties and Corrosion Behavior of Mg-Zn-Zr Alloys with Different Compositions

Alloying and Brushite Coating Improve Corrosion Resistance of Magnesium in a Simulated Physiological Environment

Mechanical Properties, Degradation Performance and Cytotoxicity of Mg–Zn–Ca Biomedical Alloys with Different Compositions

Effect of Y Contents on the Microstructure, Mechanical Properties, and Corrosion Behavior of Biomedical Mg‐0.5Zn Alloy