Abstract:The Protein-Le Chatelier (PLC) effects are investigated by using digital image correlation at a constant applied strain rate of 5.0010-3 s-1 and room temperature in Al-Mg alloys with Mg content values (wt.%) of 2.30, 4.57, 6.10 and 6.91 respectively in this study. Both the yield strength and the ultimate strength increase with increasing Mg content, which is generally called solution strengthening. Type of PLC band changes from A to B with increasing Mg content. In low Mg content (2.30%) alloy, the serration amplitude almost remains 1 MPa, while in each of high Mg content (4.57%, 6.10%, 6.91%) alloys it linearly increases with the strain increasing. The serration amplitude is found to increase with increasing Mg content and gradually reaches a saturated state. With the increase of Mg content, the period of PLC band for continuous propagation gradually reduces and the time when the PLC band location sudden jumps increases in the process of propagation. When the strain is small, the out-of-band deformation of alloy is inhomogeneous obviously. And the deformation inhomogeneity slightly decreases with increasing Mg content. DIC results indicate that the PLC bandwidth does not change with Mg content, while the maximum strain increment in the PLC band increases with increasing both Mg content and strain. Additionally, special periodic damped serrations are observed in the stress-time curve of the low Mg content (2.30%), the corresponding PLC band shows that the periodic changed serrations in the stress-time curve correspond to the transformation of the PLC band orientation. Besides, the PLC band propagates upward continuously both before and after the shift.

A method for determining r-value of aluminum sheets with the Portevin-Le Chatelier effect

The Portevin-Le Chatelier Effect in Al-Mg Alloy Investigated by Infrared Pyrometry

Characterization of Portevin–Le Chatelier Effect in Aluminum Alloy AA5052 under Strain-Controlled Tensile Test Via Digital Image Correlation and Acoustic Emission

Investigation of Portevin-Le Chatelier Effect in 5456 Al-based Alloy Using Digital Image Correlation

Anisotropic plastic flow of low/medium carbon steel plates in different loading conditions: characterization of the r- value

White-Light Digital Speckle Image Correlation Analysis of the Portevin-Le Chatelier Shearing Band in Multiscale

A Critical Review on the Portevin-Le Chatelier Effect in Aluminum Alloys

Effect of Evolution of Polycrystalline Textures on R-Value of Lf2 Aluminum Alloy

Strain-dependence of plastic strain ratio of deep-drawing aluminium-killed steel sheet

On the spatio-temporal characteristics of the Portevin-Le Chatelier effect in aluminium alloy AA5182: An experimental and numerical study

Prediction of Plastic Strain Ratio of Deep-Drawing IF Steel Sheets

A simple method enabling efficient quantitative analysis of the Portevin–Le Chatelier band characteristics

Investigation on the Sheet Metal Anisotropy by the Plane Strain Compression Method with Laminated Samples

Anisotropy Study of Thin Metallic Sheets with Strain Measurement of Digital Speckle Correlation

Portevin-Le Chatelier Effect in Al-Zn-Mg-Cu-Zr Aluminum Alloy

Acoustic Emission Inspection of Portevin-Le Chatelier Effect and Deformation Mechanisms of Two Mg–Li–Al Alloys

Experimental Investigation on the Influence of Mg Content on Portevin-Le Chatelier Effect in Al-Based Alloys by Using Digital Image Correlation

Investigation on the Portevin-Le Chatelier Deformation Bands in Al-Cu Alloys

Recurrence analysis of the Portevin-Le Chatelier effect

A Novel Method Simultaneously Eliminating Portevin-Le Chatelier Effect and Enhancing Strength in Non-Heat-treatable Al-Mg Alloys

Investigation of the Flange Earring of Deep-Drawing Aluminum Sheets by Rate-Independent Polycrystalline Plasticity Finite Element Analysis