Piezomagnetic Performance of Stress-Annealed FeAlB Alloys

M. B. de Souza Dias,C. Bormio-Nunes

DOI: https://doi.org/10.1109/TMAG.2017.2695959

IF: 1.848

2017-11-01

IEEE Transactions on Magnetics

Abstract:Two FeAlB polycrystalline alloys were stress annealed and had the piezomagnetic behavior determined before and after the stress annealing (SA). The concentration of boron is constant, 1.6% (at%). The alloys are basically formed by the phase Fe₂B dispersed in a bcc matrix. The bcc matrix can be formed of a disordered and/or ordered structure, depending on ratio of Fe:Al, that was fixed as 86Fe:14Al and 80Fe:20Al. Magnetostriction and magnetic induction were measured as a function of magnetic field and compressive stresses. The piezomagnetic coefficient <inline-formula> <tex-math notation="LaTeX">$d_{33}\equiv ~\text{d}\lambda /\text{d}H$ </tex-math></inline-formula> improvement due to SA was achieved, in which <inline-formula> <tex-math notation="LaTeX">$\lambda$ </tex-math></inline-formula> is the magnetostriction and H the applied magnetic field. SA causes the reorientation of the magnetic moment of the material creating an artificial magnetic anisotropy. The behavior of the coefficient <italic>d₃₃</italic> varies due to changes in Al content, since the magnetocrystalline anisotropy of the alloy depends on the ordering of the bcc matrix. Values of <italic>d₃₃</italic> up to 4 nm/A were reached for the polycrystalline alloy with 14% Al (at%) in an interval of compressive stresses of <inline-formula> <tex-math notation="LaTeX">$0 \le \vert \sigma \vert \le177$ </tex-math></inline-formula> MPa. This large interval of compression stress is due to the presence of the Fe₂B phase.

Physics,Materials Science