Effect of Film Thickness on Microstructural and Magnetic Properties of Lithium Ferrite Films Prepared on Strontium Titanate (001) Substrates

Kun Liu,Ruyi Zhang,Lu Lu,Jiankang Li,Songyou Zhang
DOI: https://doi.org/10.3390/coatings13122097
IF: 3.236
2023-12-17
Coatings
Abstract:Epitaxial lithium ferrite (LiFe5O8) films with different thicknesses were successfully fabricated on strontium titanate (SrTiO3) (001) substrates using the magnetron sputtering deposition technique. The microstructural and magnetic properties of the films were characterized by an advanced transmission electron microscope and a magnetic measurement device. It was found that the formation of structural defects can be influenced by the thickness of the film. In addition to misfit dislocations, orientation domains form in thinner films and twin boundaries appear in thicker films, respectively, contributing to the misfit strain relaxation in the heterosystem. The magnetic measurement showed that the thinner films have enhanced magnetization and a relatively lower coercive field compared with the thicker films containing antiferromagnetic twin boundaries. Our results provide a way of tuning the microstructure and magnetic properties of lithium ferrite films by changing the film thickness.
materials science, multidisciplinary,physics, applied, coatings & films
What problem does this paper attempt to address?
The paper primarily explores the microstructure and magnetic properties of lithium ferrite (LiFe5O8) thin films of different thicknesses on strontium titanate (SrTiO3) (001) substrates. Specifically, the study prepared lithium ferrite thin films of varying thicknesses using magnetron sputtering technology and characterized their microstructure and magnetic properties using transmission electron microscopy (TEM) and superconducting quantum interference device (SQUID). The main findings are as follows: 1. **Microstructure**: The thickness of the film affects the formation of internal defects. Oriented domains appeared in thinner films (7.5 nm), while twin boundaries formed in thicker films (30 nm). 2. **Magnetic Properties**: Thinner films exhibited higher saturation magnetization (Ms) and relatively lower coercivity (Hc), whereas thicker films showed lower Ms and higher Hc. 3. **Strain State**: Thinner films released compressive strain through oriented domains and misfit dislocations; thicker films alleviated strain through high-density twin boundaries. These results indicate that by changing the thickness of the film, the microstructure and magnetic properties of lithium ferrite films can be regulated to meet different technical application needs, such as electrodes for rechargeable lithium batteries, various components of microwave devices, and magnetic insulators in spintronics.