Phase transition, structural and magnetic parameters of vanadium-substituted Bi0.9Sm0.1FeO3 multiferroic ceramics

Mansour Al-Haj Physics Department,Mutah University,Al-Karak,Jordan

DOI: https://doi.org/10.1080/01411594.2024.2361149

2024-06-03

Phase Transitions

Abstract:The inorganic multiferroic compounds Bi 0.9 Sm 0.1 Fe 1 − x V x O 3 ( x = 0.0, 0.015, 0.03, and 0.045) were prepared by the solid-state reaction method. X-ray diffraction analysis confirmed the rhombohedral perovskite-like structure with minor traces of the impurity phases Bi 2 Fe 4 O 9 and Bi 25 FeO 40 . The lattice parameters a and c , and the volume of the hexagonal unit cell were extracted from the X-ray diffraction data and found to increase as the V 5+ content is increased. The average crystallite size was estimated to be in the range 380–415 Å. Fourier transform infrared spectroscopy confirmed the rhombohedral perovskite-like structure via the vibration bands of the octahedral FeO 6 group observed between 410 and 570 cm −1 . A differential scanning calorimeter was used to record the thermal scans which revealed that the compounds have undergone crystalline phase transitions at temperatures in the range 300–320°C. A 4.5% V + 5 substitution has shifted the transition peak by 20°C. The magnetic hysteresis loops taken at room temperature with a vibrating sample magnetometer revealed the ordinary ferromagnetic behavior. The V 5+ substitution enhanced the remanent magnetization, but the magnetic coercivity was found to fluctuate around an average value of about 1000 Oe. The compound Bi 0.9 Sm 0.1 Fe 0.955 V 0.045 O 3 exhibited the maximum remanent magnetization.

physics, condensed matter,crystallography