Effect of cobalt substitution on structural, impedance, ferroelectric and magnetic properties of multiferroic Bi_2Fe_4O_9 ceramics

S. R. Mohapatra,B. Sahu,M. Chandrasekhar,P. Kumar,S. D. Kaushik,S. Rath,A. K. Singh

DOI: https://doi.org/10.48550/arXiv.1605.01570

2016-05-05

Abstract:Structural, impedance, ferroelectric and magnetic properties were examined in multiferroic Bi_{2}Fe_{4(1-x)}Co_{4x}O_{9} (0$\leq$x$\leq$0.02) ceramics synthesized via solid-state reaction method. X-ray diffraction analysis and Rietveld refinement showed secondary phase formation (for x$\geq$0.01) which was subsequently confirmed from room temperature Raman spectroscopy study. The frequency dependence of impedance and electric modulus of the material showed the presence of non-Debye type relaxation in all the samples. The values of the activation energies calculated from imaginary impedance and modulus lie in the range of 0.92-0.99 eV which confirmed that the oxygen vacancies play an important role in the conduction mechanism. Moreover, suitable amount of Co substitution significantly enhanced the remnant polarisation (2P_{r}) from 0.1193 $\mu$C/cm^{2} (x=0) to 0.2776 $\mu$C/cm^{2} (x=0.02). Besides, room temperature M-H measurement showed improved ferromagnetic hysteresis loop for all the modified samples. The remnant magnetization (M_{r}) and coercive field (H_{c}) increased from 0.0007 emu/gm and 42 Oe for x=0 to 0.1401 emu/gm and 296 Oe for x=0.02. The improved ferroelectricity was due to Co 3d-O 2p hybridization and enhanced magnetization originated from the partial substitution of Co^{3+} ions leading to breakdown of balance between the anti-parallel sub lattice magnetization of Fe^{3+} ions.

Materials Science

What problem does this paper attempt to address?

The problem that this paper attempts to solve is: By substituting cobalt (Co) for some of the iron (Fe) ions in bismuth ferrite (Bi₂Fe₄O₉, BFO), to improve its multiferroic properties at room temperature. Specifically, the author hopes to enhance the ferroelectricity and ferromagnetism of the material by introducing cobalt, thereby overcoming the weak macroscopic magnetism and poor ferroelectric properties of BFO at room temperature.

### Main research contents include:

1. **Structural analysis**:
- The influence of cobalt substitution on the BFO crystal structure was studied through X - ray diffraction (XRD) and Rietveld refinement.
- Raman spectroscopy was used to further confirm the structural changes.

2. **Impedance and dielectric properties**:
- The frequency - dependent dielectric constant and loss tangent were studied, revealing the polarization mechanism in the material.
- The charge - transfer mechanism in the material was explored through complex impedance spectroscopy analysis, and non - Debye - type relaxation behavior was found.

3. **Ferroelectric properties**:
- The P - E loops at different cobalt - doping concentrations were measured. The results show that cobalt substitution significantly enhances the remanent polarization (\(2P_r\)), increasing from 0.1193 μC/cm² (x = 0) to 0.2776 μC/cm² (x = 0.02).

4. **Magnetic properties**:
- Through M - H loop measurement, it was found that cobalt substitution significantly increases the remanent magnetization (\(M_r\)) and coercive field (\(H_c\)), increasing from 0.0007 emu/gm and 42 Oe (x = 0) to 0.1401 emu/gm and 296 Oe (x = 0.02), respectively.
- These improvements are attributed to the structural distortion caused by cobalt substitution and the partial substitution of Co³⁺ ions, which breaks the balance of the antiparallel sub - lattice magnetization of Fe³⁺ ions.

### Conclusion:
Through cobalt substitution, the ferroelectricity and ferromagnetism of Bi₂Fe₄O₉ ceramics at room temperature are significantly improved, making it a potential room - temperature multiferroic material. These improvements are mainly attributed to Co³⁺-O²⁻ hybridization and the structural distortion caused by cobalt substitution.