Le-Zhong Li,Alexander Sokolov,Cheng-Ju Yu,Qi-Fan Li,Qi-Fan Li,Kun Qian,Vincent G. Harris
DOI: https://doi.org/10.1016/j.ceramint.2021.05.275
IF: 5.532
2021-09-01
Ceramics International
Abstract:Y3+- and Co2+-substituted Sr1-x Y x Fe12-x Co x O19 (0 ≤ x ≤ 0.50) M-type hexaferrites were synthesized using a traditional oxide ceramic process to study their structural and static magnetic properties. The well-defined M-type phase structures of the pure and Y–Co co-substituted strontium ferrites were verified via XRD analysis. When the Y–Co substitution amount (x) exceeded 0.20, the Fe2O3, Y3Fe5O12, SrFe2O4, and CoFe2O4 impurity phases coexisted in the M-type strontium hexaferrite structure. The lattice parameters a and c increased when x ≤ 0.20; however, a further increase in the Y–Co substitution caused them to decrease. The X-ray density d x initially decreased when x ≤ 0.20, and subsequently increased with a further increase in Y–Co substitution. The density of the sintered samples d s exhibited a decreasing trend with the increasing Y–Co substitution, inducing the porosity to increase. The saturation magnetization M s monotonously decreased with the increasing Y–Co substitution amount. The in-plane and out-of-plane coercivities, H c (ip) and H c (op), initially increased as x increased from 0 to 0.20. When x > 0.20, however, H c (ip) exhibited a decreasing trend; particularly, a linear decrease was observed as x increased from 0.30 to 0.50. The squareness ratio S reached its maximum (79.6%) at x = 0.20.
materials science, ceramics